Abstract:A series of rare earth-doped Fe-based oxide catalysts were prepared by co-precipitation method as Selective Catalytic Reduction (SCR) catalysts. The effects of the various rare earth species, doping amount of Sm, calcination temperature and the kind of precipitant on the deNOx activity of the catalysts were systematically investigated. The SO2 resistance performance was tested on the optimal catalyst. The catalysts have been characterized by X-ray diffraction (XRD), The X-ray photoelectron spectra (XPS), scanning electron microscopy (SEM) and Brunner Emmet Teller (BET). The results showed that the doping of Sm significantly improves the removal efficiency of Fe-based oxides. Sm0.075Fe0.925 catalyst showed the optimal deNOx performance and excellent resistance to SO2. At the optimal doping rate (0.075), the denitrification rate was close to 100% between 200 and 250 degrees C. The calcination temperature has a significant effect on the catalyst. The order of catalytic activity for different calcination temperatures was 350 degrees C approximate to 400 degrees C > 450 degrees C > 500 degrees C. The Sm0.075Fe0.925 achieved 100% the de-NOx efficiencies at calcination temperatures of 350-400 degrees C. It was also found that the deNOx performance of the catalyst prepared by using NH3 center dot H2O as the precipitating agent was better than the catalyst prepared by using (NH3)2CO3 or NaOH as the precipitating agent. Normally a small amount of SO2 would render the catalyst inactive, but the Sm0.075Fe0.925 catalyst was basically regenerated after 0.05% SO2 removal in this resistance test.

A Study of Selective Catalysis Reduction Denitration Performance and Adsorption of NH3 and NO OverγFe2O3 Catalyst

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

DRIFTS Study of Γfe2o3 Nano‐catalyst for Low‐temperature Selective Catalytic Reduction of NOx with NH3

Insight into highly efficient FeOx catalysts for the selective catalytic reduction of NOx by NH3: Experimental and DFT study

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Selective Catalytic Reduction of NOx with NH3 over Short-Range Ordered W-O-Fe Structures with High Thermal Stability

Chemical reaction kinetics of SCR of NOx over γFe2 O3 nano-catalyst

Study of the Nitric Oxide Reduction of SCR-NH3 on Γfe2o3 Catalyst Surface with Quantum Chemistry

Effects of Synthesis Conditions on Rare Earth Doped Iron Oxide Catalyst for Selective Catalytic Reduction of NOx with NH3

Selective Catalytic Reduction of NO by NH3 over MoO3 Promoted Fe2O3 Catalyst

Kinetic Study of Selective Catalytic Reduction of NOxby NH3on Magneticγ-Fe2O3Catalyst

The study of NH3‐SCR mechanism on γFe2O3 supported LaMnO3 catalyst based on DFT

Optimizing Selective Catalytic Reduction of NO with NH3 on Fe2O3/WO3 Via Redox‐Acid Synergy

In-situ DRIFTS Investigation on the Selective Catalytic Reduction of NO with NH3 over the Sintered Ore Catalyst

Mechanism Study of FeW Mixed Oxides to the Selective Catalytic Reduction of NOx with NH3: in Situ DRIFTS and MS

Selective Catalytic Reduction of NOx with NH3 over Fe Modified MOF-Derived MnOx Catalyst

Effect of Fe2O3 on ZrTiO4 Support for NH3-SCR Catalytic Performance

Study of the Adsorption of NH3 and NOx on the Nano-Γfe2o3 (001) Surface with Density Functional Theory

In Situ DRIFTS Study of the Mechanism of Low Temperature Selective Catalytic Reduction over Manganese-Iron Oxides

Low temperature selective catalytic reduction of NO with NH3 over Mn–Fe spinel: performance, mechanism and kinetic study

Effect of Fe2O3/ACF catalysts modified by non-thermal plasma on the selective catalytic reduction of NO at low temperature