Effects of Nb and Zr Alloying on the Microstructure, Mechanical Properties, and Corrosion Resistance of CoCrFeNi High-Entropy Alloys
Junxiao Liu,Zhiqin Wen,Dafu Tang,Mingze Wang,Zhenyu Wu,Bo Ma,Yu Chen,Yuhong Zhao
DOI: https://doi.org/10.1007/s11665-024-09523-2
IF: 2.3
2024-05-09
Journal of Materials Engineering and Performance
Abstract:In this study, we prepared a range of high-entropy alloys (HEAs), denoted as CoCrFeNiZr x Nb (0.4− x ) ( x = 0, 0.1, 0.2, 0.3, 0.4), through vacuum arc melting. The synergistic impact of Zr and Nb alloying on the microstructure, mechanical properties and corrosion resistance of these HEAs was investigated. Each alloy comprises a face-centered cubic (FCC) phase and the Zr(Nb)-rich Laves phase. Additionally, a novel Ni 7 Zr 2 phase precipitates in the CoCrFeNiZr 0.2 Nb 0.2 HEAs. The two distinct intermetallic phases and the FCC matrix intertwine, creating a typical hypoeutectic structure. Furthermore, the synergistic impact of solid solution strengthening, precipitation strengthening, and fine grain strengthening in CoCrFeNiZr 0.2 Nb 0.2 HEAs results in high values of yield strength and ultimate strength of 810 MPa and 1595 MPa, respectively, while maintaining a commendable compressive strain of 21.15%. Moreover, the corrosion resistance of the investigated HEAs initially rises and then declines with the continuous increase in Zr content. This trend is associated with the preferential onset of pitting corrosion in the Zr(Nb)-rich Laves phase region. Notably, the passivation film of CoCrFeNiZr 0.2 Nb 0.2 HEAs proves to be the most stable among the five HEAs due to its fine grain size and the presence of beneficial oxides. Consequently, the corrosion resistance of CoCrFeNiZr 0.2 Nb 0.2 surpasses that of the other HEAs under consideration.
materials science, multidisciplinary