Abstract:The effect of Bi2O3 on ZnO-based varistor ceramic sintered around 800 °C is still not fully understood, because most of the ceramic cannot reach full densification at this low-temperature. Therefore, (balanced) ZnO–0.5 mol% V2O5–0.5 mol% MnCO3–0.5 mol% Co2O3–0.5 mol% TiO2–xmol% Bi2O3 (x = 0, 0.01, 0.05, 0.1 and 0.2) ceramic was designed and prepared by the solid-state sintering at 800 °C. The effect of Bi2O3 variation on the microstructure and electrical nonlinearity of the sample material was studied by using methods of XRD SEM, STEM, EDS and E–J test. Bi2O3 can further activate the reaction at the interface between the V-rich liquid phase and ZnO grains during sintering. This enhanced interface reaction is the key reason to the extremely low-temperature sintering of the ceramic at 800 °C. The variation of Bi2O3 in the 0–0.2 mol% range barely influences the constituents of the ceramic, which consists of ZnO main phase and two other secondary phases: Zn3(VO4)2 and Zn2TiO4. Most of Bi2O3 tends to segregate at grain boundaries. As a result, a soaking time longer than 4 h is needed to allow Bi ions diffusing into enough grain boundaries and improving the nonlinearity of ZnO based varistor ceramic. The sample containing 0.01 mol% Bi2O3 and sintered at 800 °C for 8 h has the best properties of a 43.3 nonlinear coefficient, a 2300 V/mm breakdown voltage and a 0.13 mA/cm2 leakage current density.

Dual Effects of V2O5 in ZnO-V2O5 Varistor Ceramics During Low Temperature Sintering

Structural and electrical properties of ZnO–V2O5–TiO2–Co2O3–MnO varistor ceramics with low sintering temperature

Effect of Bi2O3 on the ZnVMnCoTiO based varistor ceramic sintered at 800 °C

Elaboration and electrical characterization of ZnO-based varistor ceramics in different sintering temperatures

Effect of the Sintering Temperature on the Electrical Properties of Y-Al-doped ZnO Varistors

Effect of Minor Bi2O3 Doping on the Microstructure and Electrical Nonlinearity of the ZnVSnO Based Varistor Ceramics

Low Temperature Sintering of Doped ZnO-V2O5 Varistors

SbVO 4 Doped ZnO–V 2 O 5 -Based Varistor Ceramics: Microstructure, Electrical Properties and Conductive Mechanism

Influence of SnO2 on ZnO–Bi2O3–Co2O3 Based Varistor Ceramics

Fabrication of High Performance ZnV Sb System Varistor Ceramics

A New Method for Studying the Conduction Mechanism of ZnO-based Varistor Ceramics

Optimization of Sintering Temperature and Doping Level of Cr2O3 in ZnO-Pr6O11-Based Varistor Ceramics

An ultralow concentration of Cr2O3 dopants driven lower temperature sintering ZnO‐based varistor ceramics

Advances in Methods of Low Temperature Liquid Phase Sintering ZnO Varistor Ceramics

Enhanced Electrical Properties of ZnO Varistor Ceramics by Spark Plasma Sintering: Role of Annealing

Two-step method fabricating high nonlinearity ZnVSb based varistors

Microstructure design and optimization of ZnO-Bi 2O 3-Sb 2O 3 based ceramic varistors

Microstructure Design and Optimization of ZnO-Bi2O3-Sb2O3 Based Ceramic Varistors

Effects of Cooling Rate on the Microstructure and Electrical Properties of Dy2O3-doped ZnO-based Varistor Ceramics

Effects of Starting Materials and V2o5 Additions on Low-Temperature Sintering and Dielectric Properties of Zinc Titanate Ceramics

Microstructure and Electrical Properties of Ga2o3 Doping on Zno Varistor Ceramics with Different Sintering Temperature