Effect of Sintering Temperature on Microstructure and Properties of Boron Aluminum Silicate Fibers

Wensheng LIU,Yin LI,Yunzhu MA,Juan WANG,Tao LUO,Shuheng XU

DOI: https://doi.org/10.14062/j.issn.0454-5648.2017.06.15

2017-01-01

Abstract:Boron aluminum silicate fibers were prepared by a sol-gel method with aluminum nitrate, boric acid, basic aluminum acetate and silica sol as raw materials. The effect of sintering temperature on the microstructure and properties of boron aluminum silicate fibers was investigated by thermogravimetry-differential thermal analysis, scanning electron microscopy, X-ray diffraction, transmission electron microscopy and Fourier transform infrared spectroscopy, respectively. The results show that when sintering temperature increases from 800 to 1000℃ , the microstructure of the fibers becomes denser and the surface and fracture become more smooth. The phases shift from amorphous to Al4B2O9 phase, and then to Al18B4O33 phase. At 1000℃, a dense, smooth and fine grain fiber can be obtained. As the temperature increases to 1300℃, the phenomenon of grain growth becomes dominant. At 1200℃, the fiber surface becomes rough and the fracture presents a crystalline morphology. At 1300℃, the phenomena of grain growth and pulverization are quite serious, and all the phases are Al18B4O33 phase with a small amount of Al4B2O9 and mullite phases. The average monofilament tensile strength and elastic modulus of fibers first increase and then decrease with increasing sintering temperature, and they reach the maximum values of 1300MPa and 138GPa, respectively, when the temperature is 1000℃ , showing a good performance consistency.