Comparison of mechanical properties in the different mixing ratio of poly methyl methacrylate
Yang Yang,Ma Xin-long,Ma Jian-xiong,Wang Zhi-gang,Wang Pei
DOI: https://doi.org/10.3969/j.issn.1673-8225.2009.42.024
2009-01-01
Abstract:BACKGROUND:Studies have been proved that different polymerization of poly methyl methacrylate(PMMA) has different mechanical properties,the mechanical properties in different types of PMMA is also different.OBJECTIVE:To explore mechanical property difference in the different mixing ratio of PMMA.DESIGN,TIME AND SETTING:The comparative observation was performed at the laboratory of Orthopaedic Biomechanics,General Hospital of Tianjin Medical University from February to May 2009.MATERIALS:Denture bases self-curing denture acrylics were made in Shanghai Coral Chemical Plant and Denture bases liquid for denture acrylics were made in Tianjin Stomatological Hospital Material Research Laboratory.METHODS:We mixed self-curing denture acrylic and liquid for denture acrylic at 1.5:1,1:1,1:1.25,1:1.5,1:1.75 and 1:2 six different kinds of hybrid scale at 25 ℃,at a speed rate of 60 times/min.When dental base acrylic resin liquid was combined with dental base acrylic resin powder,no extra dental base acrylic resin liquid was found.When adhesion feeling disappeared,it was the suitable stage of packing box.The mixed material was filled in a tooting(13 mm diameter,100 mm length).The same shape specimen of PMMA was established,and then the compression test,tension test,and three-point compression test until to yield or fracture were conducted.MAIN OUTCOME MEASURES:The compressive strength,tensile strength,deflection and elastic modulus of different mixing ratio of PMMA were measured.RESULTS:The compressive strength in the first two groups did not show significant differences(P=0.326),and was significantly greater than other groups(P < 0.01),but there were no significant differences in compressive strength in last three groups(P > 0.05).The difference of tensile strength among the first three groups was not significant(P > 0.05),but significantly greater than in the last three groups(P < 0.01).The difference was not significant among the later three groups(P > 0.05).With the mixing ratio getting smaller,the deflection was increased,which showed toughness getting better.With the mixing ratio getting smaller,the elastic modulus was getting smaller in the first five groups,which showed rigidity of specimen getting worse(P < 0.01).CONCLUSION:PMMA has high strength and rigidity,and there are significant differences in mechanical property of PMMA at various mixed ratio.With the mixing ratio getting smaller,the residual amount of liquid monomer is more after polymerization,so the compressive strength,tensile strength and elastic modulus is smaller.