Abstract:This paper was aimed to investigate the hygrothermal effects on the mechanical behavior of the double lap shear joints of Carbon/Epoxy composite laminates, which were bonded using epoxy adhesive film SY14. First, experimental method was used to evaluate the hygrothermal dependent properties of the adhesive and the static response of composite laminate double lap joints at various environment conditions. The specimens were grouped into room temperature/dry (RD), room temperature/wet (RW), elevated temperature/dry (ED) and elevated temperature/wet (EW). The wet specimens were immersed in deionized water at temperature of 90 °C for 60 h and the elevated temperature is 95 °C. Tensile tests were carried out at room temperature and elevated temperature (95 °C) in a controlled chamber. Results showed that the elastic modulus and tensile strength decreased about 24% and 27% respectively after exposure to humidity environment. And a large degradation was found when exposure to high temperature while the plasticity became notable. The failure modes of the double lap shear joints were studied by visual inspection. It was found that both adhesive and cohesive failure happened for dry specimens at room temperature. While failure modes were dominated by cohesive failure after moisture exposure and adhesive failure at elevated temperature. Second, a finite element model was utilized to simulate the damage evolution of the double lap joints. The moisture diffusion process, swelling stress and thermal stress were included. And hygrothermal dependent cohesive law was considered to study the damage evolution. It revealed that failure modes were highly dependent on the weaker strength of adhesive and cohesive. Moisture absorption caused large degradation in cohesive strength, so the failure modes were mostly cohesive failure. Elevated temperature decreases strength of adhesive seriously, so adhesive failure dominates. Good agreement was achieved between the predicted failure loads and experimental results. And the predicted failure modes were also consistent with the experimental phenomenon.

Experimental study of strain rate effects on the strength of adhesively bonded joints after hygrothermal exposure

A Systematic Study on the Failure Behaviors of Aluminum Alloy/composite Bonded Joints Exposed to Various Typical Aging Environments for Automobiles

Durability of adhesively-bonded single lap–shear joints in accelerated hygrothermal exposure for automotive applications

Effect of Hygrothermal-Mechanical Exposure on the Residual Strength of Adhesively Bonded Joints

Research on the Aging Effects of Adhesive and Composites on the Degradation Mechanism of Composite Adhesive Joints in Thermal-Humidity-Cycles for Automobiles

Research on the static strength performance of adhesive single lap joints subjected to extreme temperature environment for automotive industry

Experimental Study of Initial Strengths and Hygrothermal Degradation of Adhesive Joints Between Thin Aluminum and Steel Substrates

An Experimental Technique on the Dynamic Strength of Adhesively Bonded Single Lap Joints

Effect of Temperature on Shear Strength of Adhesively Bonded Joints for Automobile Industry

Dynamic Characteristics of Adhesive Bonded High Strength Steel Joints

Hygrothermal degradation and recoverability of mechanical properties of epoxy adhesive joints for automotives

Effect of Low-Velocity Impact on the Strength and Durability of Bonded Joint in Hygrothermal Environment

Effect of strain-rate and moisture content on the mechanical properties of adhesively bonded joints

An investigation of hygrothermal effects on adhesive materials and double lap shear joints of CFRP composite laminates

Experimental Investigation of the Mechanical Behavior of Aluminum Adhesive Joints under Mixed-Mode Loading Conditions

Effect of Hygrothermal Ageing on the Mechanical Performance of CFRP/AL Single-Lap Joints

Modelling of Deformation and Failure of Crash Toughened Adhesive Bonded Lap Shear Joints

A design of experiments assessment of moisture content in uncured adhesive on static strength of adhesive-bonded galvanized SAE1006 steel

Effect of adhesive characteristics on static strength of adhesive-bonded aluminum alloys

Strength Degradation of Adhesively Bonded Single-Lap Joints in A Cyclic-Temperature Environment Using A Cohesive Zone Model

The Effect of a Hot–Wet Environment on Adhesively Bonded Joints under a Sustained Load