Abstract:In the present work, we prepared nylon 6 crystals via crystallization of nylon from phosphoric acid by using the vapors of ammonium hydroxide as a precipitation regent. Both XRD and FTIR results demonstrate that the obtained nylon 6 sample exhibit characteristic peaks of nylon 6 in gamma form. In addition, treatment of nylon 6 in boiling water for half an hour followed by FTIR and XRD characterization shows that the obtained nylon 6 sample is in gamma form rather than in meta-stable b form. DSC characterization indicates that the nylon 6 sample exhibits two melting peaks (213 and 220 degrees C) when the sample is heated at a heating rate of 10 degrees C x min(-1). The reason for this phenomenon is that the nylon 6 sample has different lamellar thickness. To investigate the thermal behavior of the nylon 6 sample, the sample underwent the following thermal treatment procedure. First, the sample was heated to a pre-set temperature (T(s)) and kept at that temperature for an hour. Subsequently, the sample was cooled down to 100 degrees C at a cooling rate of 1 degrees C x min(-1), and then cooled down to room temperature at a cooling rate of 10 degrees C x min(-1). The treated samples were characterized by FTIR and DSC method. Experimental results show that the treated nylon 6 samples exhibit different crystalline behavior. When T. ranges from 130 to 160 degrees C, no significant changes were observed. When T(s) is 170 degrees C, a small fraction nylon 6 crystals is destroyed and recrystallized into thin lamellae in a form. As a result, a pre-melting peak appears in DSC result. The pre-melting peak moves to higher temperature and its peak area increases significantly upon increasing T(s) from 170 to 198 degrees C. When T(s) amounts to 200 degrees C, the pre-melting peak and the melting peaks 213 degrees C merge into one melting peak and two melting peaks are observed at 212 and 220 degrees C in the DSC results. FTIR spectra indicate that significant amount of crystalline nylon 6 in a form appears but the majority of crystalline phase of the sample is still gamma phase. As T(s) increases from 200 to 209 degrees C, the melting peak at lower temperature moves to higher temperature with increasing its peak area. On the other hand, the melting peak at 220 degrees C decreases in intensity but does not show any peak shift. As T(s) reaches 209 degrees C, the two melting peaks merge into one peak and FTIR results demonstrate that nylon 6 in a form becomes dominate phase in the sample. In the whole heat-treatment process, the gamma phase nylon 6 sample began to transform to a phase at the heat-treatment temperature of 170 degrees C, which is far below the melting point of the original sample (221 degrees C). This is different from the results reported in the literature, which state that gamma phase nylon 6 will not transform to alpha-phase until nylon is melt.

Preparation and Properties of Anti-static Agent for Nylon

Preparation of a Novel Stabilizer and Its Thermal‐oxidative Stabilization Effect on Polyamide 6

Effect of Thermal Oxidative Aging on the Crystallization Behavior and Properties of Nylon-6

Study of Application of Complex Antistatic Agent to PP

Preparation and Characterisation of Antistatic Nylon-6 Filled with Zno Whiskers

INFLUENCE OF THERMAL TREATMENT ON CRYSTAL MELTING BEHAVIOR AND CRYSTAL STRUCTURE OF NYLON 6 AND POLYAMIDE BLOCK COPOLYMER/NYLON 6 BLENDS

Phase stability and melting behavior of the α and γ phases of nylon 6

PREPARATION OF PERMANENT ANTI-STATIC PA6/ABS ALLOY

The preparation of permanent antistatic additive based on poly(ether- b -amide) copolymers and its modification effect on polyamide 6

Modifying the Poly Ether Ester Antistatic Agent by Carbon Nanotubes, the Antistatic Effect on Polypropylene Fibers

Investigation of Thermal Behaviors of Γ-Form Nylon 6 Prepared by Ammonia Vapor from Phosphoric Acid Solutions

Permanent Antistatic Polypropylene Based on Polyethylene Wax/polypropylene Wax Grafting Sodium Acrylate

Synthesis and Property of Antioxidative Nylon 66

Study on the Acid Resistant Properties of Bio-Based Nylon 56 Fiber Compared with the Fiber of Nylon 6 and Nylon 66

Enhanced antistatic properties of polyethylene film/polypropylene-coated non-woven fabrics by compound of hot-melt adhesive and polymer antistatic agent

Long-Chain Bio-Based Nylon 514 Salt: Crystal Structure, Phase Transformation, and Polymerization

The synthesis of a novel polymer‐type antistatic agent and its effect on the properties of polypropylene

STUDY ON NYLON 6/Nano-Tio2 AND NYLON 6/Nano-Al2o3 COMPOSITES VIA IN SITU POLYMERIZATION

The effect of polymorphism on polymer properties: crystal structure, stability and polymerization of the short-chain bio-based nylon 52 monomer 1,5-pentanediamine oxalate

Investigation of stain-resistant cationic dyeable nylon 6 modified with sodium salt of 5-sulfoisophthalic acid and polyethylene glycol

Interaction between polyamide and zinc salt]