Abstract:Rubber products generally need to have high resistance to abrasion, tear, and cutting. Filling short fiber with strong mechanical properties and forming a net in the rubber matrix is a good method to realize the above aims. In this article, ultra-high molecular weight polyethylene (UHMWPE) short fibers with a diameter of 20 μm and a length of 2 cm were filled into natural rubber (NR) to improve the tear strength of the NR. The influence of the short fiber mass fraction and vulcanization conditions on4 the mechanical properties of the composites were investigated. The results show that the milling process and vulcanization conditions are key factors in enhancing tear resistance performance. Double-roll milling and vulcanization at 143 °C for 40 min result in strong interfacial adhesion between the UHMWPE short fibers and the NR. The addition of 2 phr of UHMWPE fiber increases the tear strength of the composite material by up to 150.2% (from 17.1 kN/m to 42.8 kN/m) while also providing excellent comprehensive performance. Scanning electron microscope (SEM) imaging confirmed that the UHMWPE short fibers are dispersed in the NR matrix homogeneously, and the interface is close and compact. As a control experiment, UHMWPE resin powder was directly filled into the NR, and then the composite was vulcanized using the same process as that used for the NR/UHMWPE short fiber composite. The results show that the mechanical strength of the NR/resin powder composite exhibits minor improvement compared with NR. As there is no complicated surface modification of the UHMWPE fiber, the results reported may be helpful in improving the tear resistance of the industrially prepared rubber conveyor belts.

Effect of Formula Factors on High-temperature Tear Strength of Fluororubber

Effect of Temperature on the Tear Fracture and Fatigue Life of Carbon-Black-Filled Rubber

Effect of graphite and its surface modification on thermal conductivity of silicone rubber

Modification of Fe2O3 and its effect on the heat‐resistance of silicone rubber

The Effect of Modification of an Epoxy Resin Adhesive with ATBN on Peel Strength

Modification of Fe<sub>2</sub>O<sub>3</sub>and its effect on the heat-resistance of silicone rubber

Effects of Partial Replacement of Silicone Rubber with Flurorubber on Properties of Dynamically Cured Poly(vinylidene Fluoride)/silicone Rubber/flurorubber Ternary Blends

Effect of Compound Curing Systems on Morphology and Properties of Fluororubber/Silicone Rubber Blends

Preparation of Fluoroether Rubber Sealing Materials with Low and High Temperature Resistance

Thermal Degradation and Thermo-oxidative Aging Behavior of Vinylidene Fluoride-Containing Fluoroether Rubber

The Effect of Ceria Nanoparticles on Improving Heat Resistant Properties of Fluorosilicone Rubber

Effect of ethylene content on tear strength of silicone rubber

The effect of temperature and vulcanisation time on the thermal and mechanical properties of rubber used in tires

Effect of curatives and fillers on vulcanization, mechanical, heat aging, and dynamic properties of silicone rubber and fluororubber blends

Effects of interfacial adhesion on the rubber toughening of poly(vinyl chloride) Part 1. Impact tests

Effect of radiation sensitizer on the friction, mechanical and thermal degradation properties of electron beam cured FKM-PTFE composite

Development of fluororubber foam by supercritical N2 foaming through irradiation pre‐crosslinking and secondary cross‐linking

Impact Properties of Dynamically Vulcanized Nylon/styrene–acrylonitrile Copolymer/nitrile Rubber Blends

Accelerated Aging Behaviors and Mechanism of Fluoroelastomer in Lubricating Oil Medium

Enhancing Natural Rubber Tearing Strength by Mixing Ultra-High Molecular Weight Polyethylene Short Fibers

The Influence of Temperature and Crack Path Deviation on the Fatigue Crack Growth of a Non-crystallizing Rubber