The dynamic rheological behavior and morphology of nylon/elastomer blends
Wanjie Wang,Qiang Zheng
DOI: https://doi.org/10.1007/s10853-005-4546-3
2005-01-01
Journal of Materials Science Letters
Abstract:In the recent decades, there has been an increasing interest in preparing novel polymeric blending materials with combined and additional characteristics of each component. Having a relatively high modulus, toughness and strength, low creep, and good temperature resistance, nylons have been widely applied in the automotive industry, machinery, electronic equipment, and military applications [1]. It is well-known that blends consisting of nylon and elastomer possess excellent toughness; however, due to its highly polar amide end-groups, nylon is incompatible with elastomer. In general, it is believed that functionalization of the elastomer is a preferred approach to enhance the interfacial properties between these polymers. Research concerning nylon/functionalized elastomer blends has mostly focused on the aspects of mechanical and thermal properties. To our knowledge, only a few reports have dealt with dynamic rheological behavior of their melts [2–4]. The rheological measurements not only give much useful information for material moulding and processing, but also is an important way to characterize the structure and properties of polymer materials [5, 6]. The aim of this article is to study the influence of the graft reaction between nylon1212 and SEBS-gMA on dynamic rheological behavior and morphology of their blends. Nylon1212 (melt-flow index = 22.43 g/min) used here was obtained from Shandong Dongchen Engineering Plastic Co., Ltd., China. The elastomer, a triblock copolymer styrene-b-(ethylene-co-butylene)-b-styrene (SEBS 4033) was supplied by the Yuyao Huiju Polymer Co., Ltd. China. The maleated triblock copolymer styrene-b-(ethylene-co-butylenes)-b-styrene (SEBS-gMA) was supplied by Yuyao Yongcheng Engineering plastics Co., Ltd., China. The grafting ratio of maleic anhydride is 1.84 wt%. Both SEBS and SEBSg-MA consist of 30 wt% polystyrene end-blocks. The nylon1212/SEBS blends and nylon1212/SEBS-g-MA blends including 1 wt% antioxidant (1010) were prepared in a corotating twin-screw extruder (PRISM TES 16TC, UK) at 210 ◦C. All the samples were compression-moulded into disks of 25 mm in diameter and 1.2 mm in thickness at 180 ◦C, 50 MPa. Melt rheological tests were conducted in an ARES Rheometer