Effect of ethylene content on tear strength of silicone rubber

GUO Jian-hua,ZENG Xing-rong,LUO Kun

DOI: https://doi.org/10.3969/j.issn.1005-3174.2010.05.002

2010-01-01

Abstract:The effect of ethylene content on mechanical properties especially for tear strength of silicone rubber was researched.The crosslinking density was determined by equilibrium swelling.And the relationship between tear strength and crosslinking density was also studied.The results showed that elongation at break decreases,while 300% modulus and Shore A hardness increase with the increasing of the ethylene content from 0.03% to 0.30%.When the ethylene content is 0.15%,the tear strength and tensile strength are higher.The 50/50 silicone rubber blends with the ethylene content of 0.15% and 0.06% respectively shows highest tear strength of 45.8 kN/m.In the silicone rubber blends with the ethylene contents of 0.30% and 0.06%,the tear strength is 42.9 kN/m when the blend ratio is 4/96.The blend ratio has no effect on the mechanical properties of the blends with ethylene contents of 0.30% and 0.15%.The crosslinking structure tends to be changed from dispersive crosslinking to concentrative crosslinking by blending silicone rubber with the higher and lower ethylene content,which causes an increasing of tear strength at first and then an decreasing with the increasing of ethylene content of the blends and the crosslinking density has inverse relation with tear strength when the ethylene content is within 0.15%.