Abstract:Given the issues related to poor hydration activity, long setting time and low early strength of industrial by-product fluorogypsum (FG), the composite modifiers (Na 2 SO 4 and NaNO 2 ) were utilized to enhance its reactivity. The investigation of the mechanism involved the utilization of contemporary analytical methods, including X-ray diffraction (XRD), 1 H low-field nuclear magnetic resonance (NMR), and Scanning electron microscope and Energy Dispersive Spectrometer (SEM-EDS). The results demonstrated that the incorporation of modifiers significantly enhanced both the hydration rate and activity of fluorogypsum. The optimum concentration of the composite modifier was found to be 1.5 wt% Na 2 SO 4 and 0.5 wt% NaNO 2 . The addition of modifiers (1.5 wt% Na 2 SO 4 and 0.5 wt% NaNO 2 ) significantly shortens the setting time of FG paste, reducing it by approximately 500 min compared to the control sample. After 28 days of curing, the flexural strength and compressive strength of the fluorogypsum sample containing modifiers (1.5 wt% Na 2 SO 4 and 0.5 wt% NaNO 2 ) increased by 55.5 % (reaching 4.2 MPa) and 31.5 % (reaching 37.6 MPa), respectively. The modifiers facilitate the transformation from anhydrite (CaSO 4 , AH) to dihydrate gypsum (CaSO 4 ·2H 2 O, DH). Both NaNO 2 and Na 2 SO 4 alter the growth rates of different crystal axes during DH crystal growth, transforming them into prismatic and needle-shaped DH. The prismatic and needle-shaped DH crystals were arranged in layers, resulting in a compact structure with low hole content and few pores, which led to increased density of the hardened paste and higher strength. The current study provides evidence that the inclusion of composite modifiers greatly improves the activity of FG, making it more efficient in the field of building materials.

Modification of nature gypsum

Surface Modification of Halloysite/Sericite

Experimental study on mechanical properties of stabilized artificial organic soil

Surface Modification of Natural Fibrous Brucite with Stearic Acid

Influence of crystal-transforming agent on the performance and mechanism of α-high-strength gypsum prepared from FGD gypsum

Effects of glutaric acid, tricarballylic acid and citric acid on the morphology of α-hemihydrate gypsum: Experimental and DFT simulation studies

Effect of modifiers on crystalizing habit and mechanical strength of α-hemihydrate gypsum prepared from PG by an autoclaved method

Study on activation of fluorogypsum by sodium sulfate and sodium nitrite

Surface Modification of the Superfine Bioactive Glass Powder by Using Stearic Acid

Impact of carboxylic acid structure on α-hemihydrate gypsum crystal morphology and mechanical strength

Synthesis and Characterisation of Hemihydrate Gypsum–Polyacrylamide Composite: A Novel Inorganic/Organic Cementitious Material

Surface modification of hydroxyapatite by stearic acid: characterization and in vitro behaviors

Surface modification of nanosized biphasic alpha-TCP/HA powders

Surface modification of anhydrous phosphogypsum and its application in isotactic polypropylene

Preparation and Performance Study of Alkali-active Gypsum Mixture System

Insights into the Modification for Improving the Surface Property of Calcium Sulfate Whisker: Experimental and DFT Simulation Study

Surface Modification of Nanosized Biphasic α-TCP/HA Powders

Influence of crystal modifier on the preparation of α-hemihydrate gypsum from phosphogypsum

Mechanism of surface hydrophobicity modification of wollastonite powder

Surface functionalization of Si3N4 nanoparticles by graft polymerization of glycidyl methacrylate and styrene