Synthesis and Characterisation of Hemihydrate Gypsum–Polyacrylamide Composite: A Novel Inorganic/Organic Cementitious Material

Chen,Mi,Yang,Zheng,Wang,Record,Boulet,Wang,Albina,Huang
DOI: https://doi.org/10.3390/ma17071510
IF: 3.4
2024-03-27
Materials
Abstract:This study combined inorganic α-hemihydrate gypsum (α-HHG) with organic polyacrylamide (PAM) hydrogel to create a novel α-HHG/PAM composite material. Through this facile composite strategy, this fabricated material exhibited a significantly longer initial setting time and higher mechanical strength compared to α-HHG. The effects of the addition amount and the concentration of PAM precursor solution on the flowability of the α-HHG/PAM composite material slurry, initial setting time, and mechanical properties of the hardened specimens were investigated. The structural characteristics of the composite material were examined using XRD, FE-SEM, and TGA. The results showed that the initial setting time of the α-HHG/PAM composite material was 25.7 min, which is an extension of 127.43% compared to that of α-HHG. The flexural strength and compressive strength of the oven-dried specimens were 23.4 MPa and 58.6 MPa, respectively, representing increases of 34.73% and 84.86% over values for α-HHG. The XRD, FE-SEM, and TGA results all indicated that the hydration of α-HHG in the composite material was incomplete. The incompleteness is caused by the competition between the hydration process of inorganic α-HHG and the gelation process of the acrylamide molecules for water, which hinders some α-HHG from entirely reacting with water. The enhanced mechanical strength of the α-HHG/PAM composite material results from the tight interweaving and integrating of organic and inorganic networks. This study provides a concise and efficient approach to the modification research of hemihydrate gypsum.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to prepare a new type of inorganic/organic composite material by combining inorganic α - hemihydrate gypsum (α - HHG) with organic polyacrylamide (PAM) hydrogel and study its properties. Specifically, the research aims to: 1. **Prolong the initial setting time**: By introducing PAM hydrogel, the initial setting time of the α - HHG/PAM composite is significantly prolonged. 2. **Improve mechanical strength**: By optimizing the addition amount and concentration of PAM, improve the flexural strength and compressive strength of the composite. 3. **Explore the structural characteristics of the composite**: By means of X - ray diffraction (XRD), field - emission scanning electron microscopy (FE - SEM) and thermogravimetric analysis (TGA), study the microstructure and thermal stability of the composite. ### Main research contents 1. **Synthesis and characterization**: - Prepared PAM precursor solutions with different concentrations and mixed them with α - HHG to form α - HHG/PAM composites. - Tested the fluidity, initial setting time and mechanical properties of the composites through experiments. 2. **Performance testing**: - **Fluidity**: Studied the influence of the addition of PAM precursor solution on the fluidity of α - HHG/PAM composite slurry. - **Initial setting time**: Measured the initial setting time of the composite using a Vicat device and found that as the addition amount of PAM precursor solution increased, the initial setting time was significantly prolonged. - **Mechanical properties**: Tested the flexural strength and compressive strength of the composite through compression and bending tests, and the results showed that the mechanical properties of the composite were significantly improved. 3. **Structural analysis**: - Conducted structural analysis on the composite using XRD, FE - SEM and TGA and found that the hydration of α - HHG in the composite was incomplete, which was due to the competition between the hydration process and the PAM gelation process. ### Research conclusions By introducing PAM hydrogel, the α - HHG/PAM composite exhibits a longer initial setting time and higher mechanical strength. Specifically: - The initial setting time is extended from 11.3 minutes of pure α - HHG to 25.7 minutes, an increase of 127.43%. - The flexural strength and compressive strength are increased by 34.73% and 84.86% respectively. These results indicate that by introducing PAM hydrogel, the performance of α - HHG can be effectively improved, providing a new approach for developing high - performance inorganic/organic composite materials.