Surface modification of tricalcium phosphate for improvement of the interfacial compatibility with biodegradable polymers
Carmen Kunze,Thomas Freier,Ekaterina Helwig,Barbara Sandner,Dieter Reif,André Wutzler,Hans-Joachim Radusch
DOI: https://doi.org/10.1016/s0142-9612(02)00433-7
IF: 14
2003-03-01
Biomaterials
Abstract:The surface of tricalcium phosphate (TCP) filler particles was activated by treatment with dilute aqueous phosphoric acid. ATR-IR spectra indicated the formation of calcium hydrogen phosphate dihydrate at the surface. Oligo(lactone)s were formed by the subsequent reaction of the activated TCP with L-lactide and epsilon -caprolactone, respectively, at 150 degrees C without any additional catalysts. After extraction of the oligo(lactide), the residue of modified TCP-included calcium lactate whereas the water of crystallization of the dihydrate disappeared as shown by ATR-IR spectroscopy. Owing to the insolubility of TCP in common solvents, the analogous reaction between water-soluble disodium hydrogen phosphate dihydrate and L-lactide was used to study the kind of chemical bonds by high-resolution NMR spectroscopy. The 1H and 13C NMR spectra of the reaction product also pointed out the presence of calcium lactate. Additionally, signals were found indicating a covalent attachment of lactic acid units onto the phosphorus. For the preparation of composites, poly(L,DL-lactide) was mixed with TCP and modified TCP, respectively, in a ratio of 75/25 (w/w) and directly injection moulded into tensile test specimens at a barrel temperature of 180 degrees C. Although mechanical properties were not improved, scanning electron microscopy (SEM) indicated a better interfacial phase interaction in the composite with the modified TCP. Chemical bonds between filler and polymer matrix are assumed to be formed by transesterification reactions.
engineering, biomedical,materials science, biomaterials