Abstract:Carbonyl iron powder was coated with phosphate layer using phosphating precipitation method. The phosphated powder was dried at 60 °C for 2 h in air and heat treated by calcination at 400 and 800 °C for 3 h in air. Cylindrical specimens density of ~6.5 g.cm−3 based on iron phosphated powder calcined at 400 °C were sintered at 820, 900, 1110 °C in N2 + 10%H2 atmosphere and 1240 °C in vacuum for 30 min. The morphology and phase composition of the phosphate coating and sintered compacts were studied by scanning electron microscopy, atomic force microscopy (AFM) and X‐ray diffraction (XRD) analysis. Gelatinous morphology of dried phosphate coating (thickness of ~100 nm) containing nanoparticles of iron oxyhydroxides and hydrated iron phosphate was observed. From XRD, diffractogram indicated the presence of goethite α‐FeOOH, lepidocrocite γ‐FeOOH and ludlamite Fe3(PO4)2.4H2O. The calcined phosphate coating (thickness of ~ 400 nm) contained non‐homogeneous consistency of α‐Fe2O3 layer on iron particles, an inter‐layer of amorphous FePO4 and Fe3O4 top layer. The transformation to crystalline FePO4 structure occurred during calcination at 800 °C with the presence of α‐Fe2O3 forming a light top zone (rough morphology). The microstructure of compacts sintered in solid state at temperatures up to 900 °C has retained composite network character. A fundamental change in microstructure due to the liquid phase sintering occurred after sintering at temperatures of 1100 and 1240 °C. It was confirmed that the microstructure complex consists of spheroidized α‐Fe and α‐Fe2O3 phases surrounded by solidified liquid phase consisting various phosphate compounds. Copyright © 2013 John Wiley & Sons, Ltd.

Surface analysis of stearic acid modification for improving thermal resistant of calcium phosphate coated iron oxide yellow pigments

Surface Organic Modification Of Caco3-Tio2 Composite Pigment

Surface modification of hydroxyapatite by stearic acid: characterization and in vitro behaviors

Surface Modification of Alumina Powder Particles Through Stearic Acid for the Fabrication of Translucent Alumina Ceramics by Injection Molding

Surface modification of nanosized biphasic alpha-TCP/HA powders

Regulating the Properties of Ci Pigment Red 170 by Surface Modification Via Hydrous Alumina

Surface Modification of Nanosized Biphasic α-TCP/HA Powders

The Effect of Annealing on Microstructure and High Temperature Erosion Property of Arc-Spraying Coatings Containing Nanosized Ceramic Powders

Study on Modification of Aluminum Hydroxide

Thermal Treatment to Improve the Hydrophobicity of Ground CaCO3 Particles Modified with Sodium Stearate

Research on Dispersing Performance of Magnesium Hydroxide Modified by Stearic Acid

Mechanism of surface hydrophobicity modification of wollastonite powder

The effect of calcination on morphology of phosphate coating and microstructure of sintered iron phosphated powder

Insights into the Modification for Improving the Surface Property of Calcium Sulfate Whisker: Experimental and DFT Simulation Study

PREPARATION AND THERMAL PROPERTIES OF SiO2 COATED STEARIC ACID PHASE CHANGE MATERIALS BY LOW-TEMPERATURE ONE-STEP SOLID-STATE CHEMICAL REACTION

Effects of Surface Modification with Stearic Acid on the Dispersion of Some Inorganic Fillers in PE Matrix

Adsorption behavior of the surface conditioning agent particles on the surface of high-strength steel

Evolution of phosphate coatings during high-temperature annealing and its influence on the Fe and FeSiAl soft magnetic composites

Influence of Surface Modification of Srfe12o19 Particles with Oleic Acid on Magnetic Microsphere Preparation

Preparation and characterization of organic modified calcium carbonate by sodium stearate (or sodium oleate) using wet method

Surface Modification of Long Afterglow Sr<sub>4</sub>Al<sub>14</sub>O<sub>25</sub>: Dy,Eu Phosphor by Silica Coating