Abstract:Due to their special appearance, spherical α‐Al2O3 nanoparticles play an important role for obtaining high performance structural and functional ceramics. However, there are still problems such as easily agglomerates to form worm‐like structures at high temperatures and difficult availability of spherical nanoparticles. In this study, spherical α‐Al2O3 nanoparticles with high dispersion were prepared by combination of microwave hydrothermal method and addition of nano‐Al particles as seeds. Firstly, spherical amorphous alumina precursors were synthetized by microwave hydrothermal method at 100°C for 30 min using Al2(SO4)3∙18H2O, Al(NO3)3∙9H2O and urea as raw materials, and then, spherical α‐Al2O3 nanoparticles with diameter of about 66 nm were acquired after calcined the precursor at 1050°C for 90 min by adding nano‐Al seeds, which reduced the calcination temperature by 50°C and holding time by 30 min compared to that without seeds. Kinetic analysis shows that 5 wt.% nano‐Al seeds can reduce the activation energy of crystalline transition of γ‐Al2O3 to α‐Al2O3 from 516.51 kJ/mol to 474.37 kJ/mol. Moreover, the microscopic mechanism of nano‐Al particles as seeds was investigated. The characterizations of sintering properties show that spherical α‐Al2O3 nanoparticles facilitate the acquisition of uniform microstructure for resulting ceramic and the fracture modes include both intergranular and transgranular fracture.This article is protected by copyright. All rights reserved

Synthesis of α-Al2O3 nanoparticles with uniform size distribution by stearic acid-assisted mechanochemical method

Effect of Stearic Acid on Aggregates in Process of Preparation of Ultrafine α-Al2O3 Powders

Preparation of α-Al2O3 by low-temperature calcining γ-Al2O3 with α-phase seed in-situ obtained by ball milling

α-Calcium Sulfate Hemihydrate Nanorods Synthesis: A Method for Nanoparticle Preparation by Mesocrystallization

One-step Mechanochemical Transformation of Bulk Pseudo-Boehmite into Nanosized Α-Al2o3

Effect of composite additives on phase transition and dispersibility of α-Al2O3

Lowering the synthesis temperature of α‐Al2O3 by increasing the content of pentacoordinate aluminum in the precursors

Nano-sized amorphous alumina particles obtained by ball milling ZnO and Al powder mixture

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Estimating of Stearic Acid Dosage Using Self-Propagating Combustion Method in Synthesis of Nanocrystalline Ceo2 Powders

Preparation of Near-Spherical α-Al2O3 Particles by Enhanced Precipitation of Gibbsite from Sodium Aluminate Solution Using Highly Dispersed Al2O3 as Seeds

Preparation of spherical α‐Al 2 O 3 nanoparticles by microwave hydrothermal synthesis and addition of nano‐Al seeds

The Effect of Stearic Acid on Microstructure and Properties of (Ti2AlC + Al2O3)p/TiAl Composites

Controllable Preparation Conditions of Monodisperse γ-Al2O3 Nanoparticles

Size-controlled synthesis of nano α-alumina particles through the sol–gel method

Size-controlled synthesis of alumina nanoparticles from aluminum alkoxides

An Α-Fe2o3 Powder of Nanosized Particles Via Precursor Dispersion

Preparation and magnetic properties of Al2O3-coated acicular α-Fe particles

Synthesis and sintering behavior of a nanocrystalline α-alumina powder

The Effects of Surfactants on the Granularity of the Ha Powder Synthesized by Mechanochemistry

Enhancing the combustion of nAl with AlF 3 coating: gas–solid reaction mechanism for reducing combustion agglomeration of Al powder