Abstract:We present a new convenient and efficient "grafting from" method to obtain well defined polystyrene (PS) silica nanoparticles. The method, based on Nitroxide-Mediated Polymerization (NMP), consists to bind covalently the alkoxyamine, which acts as initiator controller agent, at the silica nanoparticles surface in two steps. The first step is a reaction between the aminopropylsilane and the silica particles in order to functionalize the particles surface with amino group. In a second step, the initiating-controlling alkoxyamine moiety is introduced via an over grafting reaction between the amino group and the N-hydroxysuccinimide based MAMA-SG1 activated ester. To simplify both their chemical transformation and the polymerization step, the native silica particles, initially dispersed in water, have been transferred in an organic solvent, the dimethylacetamide, which is also a good solvent for the polystyrene. The synthesis parameters have been optimized for grafting density, conversion rates, and synthesis reproducibility while keeping the colloidal stability and to avoid any aggregation of silica particles induced by the inter-particles interaction evolution during the synthesis. After synthesis, the final grafted objects have been purified and the non-grafted polymer chains formed in the solvent have been washed out by ultra filtration. Then the particles have been studied using Small angle Neutron Scattering (SANS) coupled to neutron contrast variation method. To optimize the contrast conditions, both hydrogenated and deuterated monomers have been used for the synthesis. A refined fitting analysis based on the comparison on two models, a basic core-shell and the Gaussian Pedersen model, enables us to fit nicely the experimental data for both the hydrogenated and deuterated grafted case. Differences are seen between grafting of normal or deuterated chains which can be due to monomer reactivity or to neutron contrast effect variations. The synthesis and the characterization method established in this work constitute a robust and reproducible way to design well defined grafted polymer nanoparticles. These objects will be incorporated in polymer matrices in a further step to create Nanocomposites for polymer reinforcement.

Surface functionalization of Si3N4 nanoparticles by graft polymerization of glycidyl methacrylate and styrene

Surface grafting onto SiC nanoparticles with glycidyl methacrylate in emulsion

Raft Grafting Polymerization of Mma/St from Surface of Silicon Wafer

Behavior of epoxy resin filled with nano-SiO<sub>2</sub> treated with a Eugenol epoxy silane

Controlled Grafting of Well-Defined Epoxide Polymers on Hydrogen-Terminated Silicon Substrates by Surface-Initiated Atrp at Ambient Temperature

Grafting of Polystyrene Onto A Nanometer Silica Surface by Microemulsion Polymerization

Controlled Grafting of Well-Defined Polymers on Hydrogen-Terminated Silicon Substrates by Surface-Initiated Atom Transfer Radical Polymerization

Synthesis of Composite Nanoparticles Bearing Epoxy Functional Groups: Encapsulation of Silica by Emulsion Polymerization of Gma

Encapsulation of silica nanoparticles by redox-initiated graft polymerization from the surface of silica nanoparticles.

In Situ Formation of Silica Nanoparticles Decorated with Well-Defined Homopolymers and Block Copolymers

Functionalized Si3N4 nanoparticles modified with hydrophobic polymer chains by surface-initiated atom transfer radical polymerization (ATRP)

Preparation of acrylate polymer/silica nanocomposite particles with high silica encapsulation efficiency via miniemulsion polymerization

Preparation of Epoxy‐functionalized Polystyrene/silica Core–shell Composite Nanoparticles

Polystyrene grafting from silica nanoparticles via Nitroxide-Mediated-Polymerization (NMP): synthesis and SANS analysis with contrast variation method

ANCHORING OF AZO INITIATOR AND GRAFTING OF POLY(METHYL METHACRYLATE) ONTO NANAOMETER SILICA

Mechanism and Process of the Redispersion of the Aggregated Nano-Sio2 Particles During Emulsion Polymerization of Styrene

Polymer-Grafted Nanoparticles Prepared by Surface-Initiated Polymerization: the Characterization of Polymer Chain Conformation, Grafting Density and Polydispersity Correlated to the Grafting Surface Curvature

End‐grafting Copolymers of Styrene and 4‐vinylpyridine on an Interacting Solid Surface

Surface modification of Si3N4 ceramic powders by emulsion polymerization

Biomimic preparation of highly dispersible silica nanoparticles based polymer nanocomposites

The Influence of Surface Functional Groups of Nano-Sio2 on Nylon 6 in Situ Polymerization