Abstract:Hard and brittle iron intermetallic compounds (IMCs) will be formed during solidification due to the existence of iron element in Aluminum alloy. These IMCs will cause cracks or fractures in the material, which can deteriorate the mechanical properties. Synchrotron X-ray tomography were used to study the real time formation and growth dynamics of IMCs in Al-10 wt.%Si-1 wt.%Fe alloy during solidification under transverse magnetic field (TMF). The results indicated that the precipitation behavior of IMCs was significantly affected by 0.07 T TMF. The IMCs were observed to form only on the periphery of the sample under TMF, comparing with random distribution without TMF. In addition, the growth dynamics of IMCs were also affected by TMF. When solidified without TMF, an explosive nucleation and growth of IMCs was presented at the intermediate solidification stage, where a large number of fine IMCs precipitated at the entire regions of the sample. In contrast, the IMCs located at the periphery areas were observed to grow steadily under TMF. The growth rate and formation mechanism of IMCs were also quantified and revealed, showing difference with and without TMF. The tip growth rate was relatively stable when solidified with TMF, while an accelerating growth stage was presented when TMF is absent. The discrepancy in precipitation behavior of IMCs could be best explained as the convection of the melt resulted from the applied TMF. The TMF was demonstrated to generate a directional flow with a velocity of ∼3.3 mm/s. The flow was supposed to drive the Fe solute from the center to the edge of the sample, providing enough Fe solute for IMCs to nucleate and grow on the surface of the sample. In addition, due to the influence of TMF induced flow on the distribution of Fe solute and temperature, the morphology and tip growth rate of IMCs were also affected. The result presented in current study provides the possibility to regulate the precipitation behavior of Fe-rich IMCs in Al alloys. The imposed TMF also shows the potential application in Fe removal by driving the Fe solute to the surface of sample in Al alloys.

Bubble-induced Formation of New Intermetallic Compounds in an Al–Mn Alloy During Heating Observed by Synchrotron Radiography

Bubble Growth, Intermetallic Compounds Dissolution and Their Interactions During Heating of an Al-5wt.%Mn Alloy by In-Situ Synchrotron Radiography

Growth Behaviors of Bubbles and Intermetallic Compounds in Solidifying Al-5 Wt.% Mn Alloy

In Situ Observation on Bubble Behavior of Solidifying Al-Ni Alloy under the Interference of Intermetallic Compounds

Microstructural Evolution and Growth Behavior of Intermetallic Compounds at the Liquid Al/solid Fe Interface by Synchrotron X-ray Radiography

Observation of Bubble-Involving Spontaneous Gas Dissolution in Superheated Al Alloy Melt

In-situ Study on Hydrogen Bubble Evolution in the Liquid Al/solid Ni Interconnection by Synchrotron Radiation X-ray Radiography

In Situ Observation on the Formation of Intermetallics Compounds at the Interface of Liquid Al/solid Ni

4D synchrotron X-ray tomographic study of the influence of transverse magnetic field on iron intermetallic compounds precipitation behavior during solidification of Al–Si–Fe alloy

In situ X-ray imaging of α-Al(FeMn)Si grain evolution during solidification of an Al-Si alloy with electromagnetic stirring

Understanding Homogeneous Nucleation in Solidification of Aluminum by Molecular Dynamics Simulations

Imaging of Structure Evolution in Solidifying Al–Bi Immiscible Alloys by Synchrotron Radiography

Faceted-Nonfaceted Growth Transition and 3-D Morphological Evolution of Primary Al6mn Microcrystals in Directionally Solidified Al-3 At.% Mn Alloy

Study of Faceted Al2Cu Intermetallic Compounds Growth During Solidification under Strong Static Magnetic Field Via X-ray Computed Tomography

In Situ Study on the Growth Behavior of Primary Al 3 Ni Phase in Solidifying Al–Ni Alloy by Synchrotron Radiography

Intermittent nucleation and periodic growth of grains under thermo-solutal convection during directional solidification of Al-Cu alloy

Observation of Bi Coarsening and Dissolution Behaviors in Melting Al–Bi Immiscible Alloy

Machine learning-augmented modeling on the formation of Si-dominated Non- β′′ early-stage precipitates in Al-Si-Mg alloys with Si supersaturation induced by non-equilibrium solidification

Research on homogeneous nucleation and microstructure evolution of aluminium alloy melt

Non-equilibrium Alloy Formation in the Ag–Zr System by Ion Beam Mixing

Heterogeneous Nucleation at Inoculant Particles in a Glass Forming Alloy: an Ab Initio Molecular Dynamics Investigation of Interfacial Properties and Local Chemical Bonding