Abstract:A series of high-entropy alloys (HEAs) containing nanoprecipitates of varying sizes were successfully prepared by a non-consuming vacuum arc melting method. In order to study the irradiation evolution of helium bubbles in the FeCoNiCr-based HEAs with γ' precipitates, samples were irradiated with 100 keV helium ions to a fluence of 5 × 10 20 ions/m 2 at 293 K and 673 K. And the room temperature irradiated samples were annealed at different temperatures to examine the diffusion behavior of helium bubbles. Transmission electron microscope (TEM) was employed to characterize the structural morphology of precipitated nanoparticles and the evolution of helium bubbles. Experimental results reveal that nanosized, spherical, dispersed, coherent and ordered L1 2 -type Ni 3 Ti γ' precipitations were introduced in FeCoNiCr(Ni 3 Ti) 0.1 HEAs by means of ageing treatments at temperatures between 1073-1123 K. Under the ageing treatment conditions applied in this work, γ' nanoparticles were precipitated in FeCoNiCr(Ni 3 Ti) 0.1 HEAs with average diameters of 15.80 nm, 37.00 nm and 62.50 nm, respectively. The average sizes of helium bubbles observed in samples after 673 K irradiation were 1.46 nm, 1.65 nm and 1.58 nm, respectively. The improvement in the irradiation resistance of FeCoNiCr(Ni 3 Ti) 0.1 HEAs was evidenced by the diminution in bubbles size. Furthermore, FeCoNiCr(Ni 3 Ti) 0.1 HEAs containing γ' precipitates of 15.8 nm exhibited the minimum size and density of He bubbles, which can be ascribed to the considerable helium trapping effects of heterogeneous coherent phase boundaries. Subsequently, annealing experiments conducted after 293 K irradiation indicate that HEAs containing precipitated phases exhibit smaller apparent activation energies (E a ) for helium bubbles, resulting in larger helium bubble sizes. This study provides guidance on improving the irradiation resistance of L1 2 -strengthened high-entropy alloys.

Effects of composition complexity of single-phase concentrated solid solution alloys on He bubbles behavior

Effects of temperature on helium cavity evolution in single-phase concentrated solid-solution alloys

Intergranular Fracture Induced by Helium Bubbles Segregation in NiFe Single-Phase Concentrated Solid Solution Alloys

Bubble formation in helium-implanted nanostructured ferritic alloys at elevated temperatures

Evolution of helium bubbles in FeCoNiCr-based high-entropy alloys containing γ' nanoprecipitates

The Effect of Chemical Ordering and Coherent Nanoprecipitates on Bubble Evolution in Binary-Phase Vanadium Alloys after He Ion Irradiation

He Behavior in Ni and Ni-based Equiatomic Solid Solution Alloy

Composition Complexity Enhances the He-retaining Ability of Zr-based MPEAs

The Impact of Vacancy Formation Energies on the Nucleation and Growth of Helium (he) Bubbles in Low-Activation Multicomponent Vanadium-Based Alloys

Effects of minor alloying addition on He bubble formation in the irradiated FeCoNiCr-based high-entropy alloys

Interaction Between Recrystallization and Helium Behavior in Cold-Rolled Nickel

Effects of Temperature on Helium Bubble Behaviour in Fe–9Cr Alloy

Effect of silicon addition on the microstructures, mechanical properties and helium irradiation resistance of NiCoCr-based medium-entropy alloys

First-Principles Study of Helium Trapping in Carbide Precipitates (cr23c6) in Ferritic-Martensitic Steels

Helium Bubble Evolution in a Zr–Sn–Nb–Fe–Cr Alloy During Post-Annealing: an In-Situ Investigation

Temperature-dependent helium induced microstructural evolution in equiatomic NiCo and NiFe concentrated solid solution alloys

Theoretical study on the influence of Cr, Mo, and W alloying additions on the helium behavior in nickel

Effects of Grain Boundaries and Nano-Precipitates on Helium Bubble Behaviors in Lanthanum-Doped Nanocrystalline Steel

A multi-perspective study on the evolution behavior of helium bubbles in FeCrVTi x medium-entropy alloys

Theoretical Combined Experimental Study of Unique He Behaviors in High-Entropy Alloys

Improvement of helium swelling resistance of nickel-based alloy via proper SiCNP dispersion