Abstract:Freezing-thawing (F-T) cycle is one of the main reason of concrete damage in cold regions. F-T cycle mainly lead to degradation of macroscopic mechanical properties of concrete by changing the number of micropores, mesopores and macropores, and causing severely damage to its internal texture. The variations of the physical and mechanical properties of concrete sample with different inclination angle of internal flaw exposed to different F-T cycles (0, 10, 30 and 50 cycles) under unconfined compression condition was deeply investigated based on the acoustic emission (AE) and nuclear magnetic resonance (NMR) technology. The evolution of the internal cracks are tracked in real-time by AE monitoring systems during the entire test process. Meanwhile, the micro-structure of the concrete sample after F-T cycle treatment is microscopically observed with T2 distribution by low-field nuclear magnetic resonance. The results show that the peak strength of concrete decreases with the increasing F-T cycles and increases as the increasing inclination angle of prefabricated flaw. The elastic modulus decreased gradually with the increase of F-T cycles. The elastic modulus of the sample without F-T cycles treatment increases with the increase of inclination angle of prefabricated flaw. As the flaw inclination angle increases from 0° to 90°, the F-T cycles increases from 0 to 50, the peak strain shows an obvious discreteness without monotone change. When the number of F-T cycle reaches 50, concrete blocks fall off from the sample surface. A continuum damage model considering F-T damage from different pore size is finally introduced to describe the damage evolution of concrete during compression test. The research results can be used to quantitatively evaluate the strength of concrete samples treated by F-T cycle without mechanical tests.

Characterization Of Microstructural Damage Evolution Of Freeze-Thawed Shotcrete By An Integrative Micro-Ct And Nanoindentation Statistical Approach

Multiscale Modeling of Damage and Fracture in Freeze-Thawed Shotcrete

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Dependence of Chloride Ion Diffusivity on Evolution of Pore-Structures in Freeze-Thawed Shotcrete: Multiscale Characterization and Modeling

Microscopic Characterization of Concrete Durability Using Nano-Indentation Tests

Microstructural Damage Evolution And Its Effect On Fracture Behavior Of Concrete Subjected To Freeze-Thaw Cycles

Microstructural Damage Characterization Of Concrete Under Freeze-Thaw Action

Experimental Investigation of the Deformational Behavior of the Interfacial Transition Zone (itz) in Concrete During Freezing and Thawing Cycles

Study on Freezing-Thawing damage mechanism and evolution model of concrete

Nanoindentation-based Micromechanical Characterisation of Ultra-High-performance Concrete Exposed to Freezing–thawing

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Durability of Air-Entrained Shotcrete Exposed to Cyclic Freezing and Thawing Effect

Micromechanical modeling of frozen concrete by micro-deformation of multi-phase composite material

Investigation on Degradation of Micromechanical Properties of Interfacial Transition Zone of Ultra-High Performance Concrete under Freeze-Thaw Cycles

Influence of Microstructure on Dynamic Mechanical Behavior and Damage Evolution of Frozen-Thawed Sandstone Using Computed Tomography

Multiscale Prediction of Thermal Damage for Hybrid Fibers Reinforced Cementitious Composites Blended with Fly Ash at High Temperatures

Structural behaviors evaluation of RC beam under frost damage - A methodology with meso-macro material/bond simulation and integrating into structural analysis

Change of the Coefficient of Thermal Expansion of Mortar Due to Damage by Freeze Thaw Cycles

Development of Micro and Macro Fracture Properties of Cementitious Materials Exposed to Freeze-Thaw Environment at Early Ages

Strengthening Mechanism of Fracture Properties by Nano Materials for Cementitious Materials Subject to Early-Age Frost Attack

Influence of construction-induced damage on the degradation of freeze—thawed lightweight cellular concrete