Abstract:Shotcrete is often used to repair overhead and vertical concrete surfaces. However, the material mismatch between the concrete substrate and shotcrete overlay makes the shotcrete-to-concrete interface bond weaker and more susceptible to damage. Hence, the performance of such composite bi-material structures depends on the soundness of interface bond. Although substrate surface preparation before the shotcrete application improves the short-term bond properties, cyclic freeze-thaw weathering in colder regions could adversely affect the longterm bond performance in such composite systems. Nevertheless, the long-term freeze-thaw durability of concrete-to-shotcrete interface bonds is not well understood.In order to address this issue, this study evaluates the long-term freeze-thaw durability of the concrete-toshotcrete interface bonds under tensile loads. The freeze-thaw cycle temperature is varied between -0.4 degrees F (-18 degrees C) and 39.2 degrees F (4 degrees C) at a frequency of about eight cycles per day. Tensile bond tests are performed on fifteen samples for each of the four surface preparation techniques at 100, 200, and 300 F/T cycles. Three different substrate surface preparation techniques, namely, chipping, pressure washing, and sandblasting, are compared with the tensile bond strength of specimens with unprepared surfaces. A probabilistic damage model based on three-parameter Weibull distribution is constructed to establish a relationship between the life (i.e., the number of freeze-thaw cycles) and the damage parameter.The results indicate that the tensile bond strength varies in descending order as chipping, pressure washing, sandblasting, and unprepared surfaces, indicating the importance of surface preparation in concrete repairs. The predicted results based on the Weibull distribution for the tensile bond strengths at a 50% reliability level are consistent with the experimental ones. Overall, the proposed probabilistic damage model is competent in evaluating the freeze-thaw durability and predicting the life of shotcrete-concrete interface bonds.

Durability of Air-Entrained Shotcrete Exposed to Cyclic Freezing and Thawing Effect

Experimental Study on the Performance Decay of Permeable Asphalt Mixture in Seasonally Frozen Regions under Freeze-Thaw Cycles

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Freeze-thaw Durability of Shotcrete-Concrete Interface Bonds in Tension

Multiscale Modeling of Damage and Fracture in Freeze-Thawed Shotcrete

Probabilistic damage modeling and service-life prediction of concrete under freeze–thaw action

Cohesive Fracture and Probabilistic Damage Analysis of Freezing–thawing Degradation of Concrete

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Mesoscale Simulation of Fatigue Behavior of Concrete Materials Damaged by Freeze-Thaw Cycles

Characterization Of Microstructural Damage Evolution Of Freeze-Thawed Shotcrete By An Integrative Micro-Ct And Nanoindentation Statistical Approach

Dependence of Chloride Ion Diffusivity on Evolution of Pore-Structures in Freeze-Thawed Shotcrete: Multiscale Characterization and Modeling

Flexural Behaviour of Reinforced Concrete Beams under Freeze–thaw Cycles and Sustained Load

Flexural behaviour of reinforced concrete members subjected to freeze-thaw cycles

Environmental Factors Influencing The Durability Of Concrete Structures In Frost Environments

Behavior of Air-Entrained Concrete after Freeze-Thaw Cycles

Experimental Investigation of the Deformational Behavior of the Interfacial Transition Zone (itz) in Concrete During Freezing and Thawing Cycles

Structural behaviors evaluation of RC beam under frost damage - A methodology with meso-macro material/bond simulation and integrating into structural analysis

Study on Freezing-Thawing damage mechanism and evolution model of concrete

Evaluation of fracture behavior of high-strength hydraulic concrete damaged by freeze-thaw cycle test

Evaluation of freeze-thaw damage on concrete material and prestressed concrete specimens

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles