Abstract:Freezing-thawing (F-T) cycle is one of the main reason of concrete damage in cold regions. F-T cycle mainly lead to degradation of macroscopic mechanical properties of concrete by changing the number of micropores, mesopores and macropores, and causing severely damage to its internal texture. The variations of the physical and mechanical properties of concrete sample with different inclination angle of internal flaw exposed to different F-T cycles (0, 10, 30 and 50 cycles) under unconfined compression condition was deeply investigated based on the acoustic emission (AE) and nuclear magnetic resonance (NMR) technology. The evolution of the internal cracks are tracked in real-time by AE monitoring systems during the entire test process. Meanwhile, the micro-structure of the concrete sample after F-T cycle treatment is microscopically observed with T2 distribution by low-field nuclear magnetic resonance. The results show that the peak strength of concrete decreases with the increasing F-T cycles and increases as the increasing inclination angle of prefabricated flaw. The elastic modulus decreased gradually with the increase of F-T cycles. The elastic modulus of the sample without F-T cycles treatment increases with the increase of inclination angle of prefabricated flaw. As the flaw inclination angle increases from 0° to 90°, the F-T cycles increases from 0 to 50, the peak strain shows an obvious discreteness without monotone change. When the number of F-T cycle reaches 50, concrete blocks fall off from the sample surface. A continuum damage model considering F-T damage from different pore size is finally introduced to describe the damage evolution of concrete during compression test. The research results can be used to quantitatively evaluate the strength of concrete samples treated by F-T cycle without mechanical tests.

Influence of Water Pressure on the Mechanical Properties of Concrete after Freeze-Thaw Attack under Dynamic Triaxial Compression State

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Effect of Different Moisture Content on Mechanical Parameters of Red Clay Under Freeze-Thaw Cycle

Effect of water pressure on mechanical behavior of concrete under dynamic compression state

Study on Mechanical Properties of Deep Expansive Soil and Coupling Damage Model of Freeze–Thaw Action and Loading

Effect of freeze–thaw cycles on the stress–strain curves of unconfined and confined concrete

Influence of High Water Pressure on Static and Dynamic Compressive Strength of Concrete

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Experimental Study on Complete Compressive Stress-Strain Curve of Concrete Subjected to Freeze-Thaw Cycles

Uniaxial Dynamic Tensile Properties of Hydraulic Concrete after Freezing-Thawing Cycles

Behavior of Concrete in Water Subjected to Dynamic Triaxial Compression

Flexural behaviour of reinforced concrete members subjected to freeze-thaw cycles

Experimental Study on Properties of Fully-Graded Concrete under Uniaxial Dynamic Compressive Stress State after Freezing-Thawing Cycles

Influence of free water on the quasi-static and dynamic strength of concrete in confined compression tests

Flexural Behaviour of Reinforced Concrete Beams under Freeze–thaw Cycles and Sustained Load

Study on Freezing-Thawing damage mechanism and evolution model of concrete

Influence of damage degree on the degradation of concrete under freezing-thawing cycles

Experimental Study of Dynamic Biaxial Compressive Properties of Full Grade Aggregate Concrete after Freeze Thaw Cycles

STRESS-STRAIN RELATIONSHIP OF CONCRETE AFTER FREEZING-THAWING CYCLES