Abstract:Morphology and crystalline-phase control of titanium dioxide is a crucial issue in the study of photocatalytic activity. Here, we present a facile synthetic path combing the solgel method with solvothermal treatment to form hybrid mesoporous and microporous TiO2. The TiO2 precursor was obtained by the solgel method, and this was self-assembled into mesopores and micropores by NH4F corrosiveness on the surface of TiO2 under hydrothermal conditions. Powder X-ray diffraction (XRD), thermogravimetric analysis and differential scanning calorimetry (TGA/DSC), X-ray photoelectron spectroscopy (XPS), N-2 adsorption measurements, transmission electron microscopy (TEM) and Raman spectroscopy were used to characterise the titania powders. The results reveal that NH4F not only improved the formation of the crystallised anatase phase but also served as a corrosive agent modified on the surface of TiO2 precursors. Defective voids among these nanoparticles formed micropores by hydrothermal reaction of NH4F and TiO2 over a long time. When the NH4F concentration was 1.0 mol.L-1, micropores became dominant,and few mesopores were obtained, and this results in a smaller average pore size. Thus, mesoporous and microporous structures were formed. Furthermore, these crystallised mesoporous and microporous anatase titania nanoparticles with uniform structure and high surface area have a higher photocatalytic activity for azo dye degradation under near UV irradiation.

Synthesis of Nanostructured TiO2 Particles in Room Temperature Ionic Liquid and Its Photocatalytic Performance

Preparation and Properties of TiO2/Bentonite Composite Photocatalytic Materials at Room Temperature

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Preparation and Properties of Nanostructure Anatase Tio2 Monoliths Using 1-Butyl-3-methylimidazolium Tetrafluoroborate Room-Temperature Ionic Liquids As Template Solvents

Photocatalytic Activity of Different Shape-controlled TiO2 Nanoparticles Toward Methyl Orange

Photocatalytic activity of TiO 2 nanorods, nanowires and nanoflowers filled with TiO 2 nanoparticles

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Sol-Gel Preparation and Characterization of High Activity Titanium Dioxide Nanocrystalline Photocatalyst

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Controlled hydrolytic synthesis of nanosized titania and evaluation of photodegradation of methyl orange

Photocatalytic Degradation of Methyl Orange by Using Different Shape-controlled TiO2 Micro-crystals

Preparation and Properties of TiO2/illite Composites Synthesized at Different Hydrothermal Ph Values

Synthesis and Photocatalytic Property of TiO<sub>2</sub> Particles Preparated in the Solvothermal Method

Synthesis of Controllable Crystalline Nano-Tio2 at Low Temperature

Synthesizing of nanosize TiO2 and its high photocatalysis performance under visible light irradiation

Synthesis of Nano-Sized SrTiO3 Photocatalyst by Sol-Gel Method

Low-Temperature Synthesis of Nanostructured TiO2 Particles and Their Photocatalytic Oxidation Activity

Synthesis and Characterization of TiO_2 Nano-crystalline with Different Morphologies by Low-temperature Hydrothermal Method

Anatase-TiO2 nano-particle preparation with a micro-mixing technique and its photocatalytic performance

Synthesis of titanium dioxide nano-powder via sol–gel method at ambient temperature