Abstract:TiO2-coated activated carbon (AC) grain (TiO2/AC) was prepared through hydrolytic precipitation of TiO2 from Tetrabutylorthotitanate and following heat treatment. The TiO2/AC was characterized by BET, SEM, XRD and optical absorption spectroscopy. The samples were employed as catalysts for methyl orange photocatalytic oxidation degradation in aqueous suspension, used as probe reaction. The kinetics of methyl orange photodegradation was analyzed. The results indicate that BET surface area of TiO2-coated ACs decreased drastically in comparison with the original AC with increasing TiO2 coatings by more than 1 doped cycle. Nano-TiO2 particles were dispersed on the AC with the size of 20–40nm. Crystalline TiO2 doped onto AC was from anatase to rutile with increase of heat-treatment temperature. The TiO2/AC was shown high photoactivity for the photodegradation of methyl orange (MO) dyestuff in aqueous solution under UV irradiation. The kinetics of photocatalytic MO dyestuff degradation was found to follow a pseudo-first-order rate law. It was observed that the presence of the AC enhanced the photoefficiency of the titanium dioxide catalyst. Different amount of TiO2 coatings induced different increases in the apparent first-order rate constant of the process. The kinetic behavior could be described in terms of a modified Langmuir–Hinshelwood model. The values of the adsorption equilibrium constants for the organic molecules, KC, and for the rate constants, kc, were certainly dependent on TiO2 content. At 47wt% TiO2 coatings with the highest rate constant, the KC and kc was 0.1116lmmol−1 and 0.1872mmoll−1min−1, respectively. The mechanism of methyl orange degradation was discussed in terms of the titanium dioxide photosensitization by the AC.

Photocatalytic Degradation of Methyl Orange by Using Different Shape-controlled TiO2 Micro-crystals

Photocatalytic Activity of Different Shape-controlled TiO2 Nanoparticles Toward Methyl Orange

Preparation of TiO_2/SiO_2 and Photo-Catalytic Degradation of Methyl-Orange

Exploration of the active species in the photocatalytic degradation of methyl orange under UV light irradiation

Controlled hydrolytic synthesis of nanosized titania and evaluation of photodegradation of methyl orange

Enhancing photocatalytic degradation of methyl orange by crystallinity transformation of titanium dioxide: A kinetic study

Preparation of TiO2 Nanofilm Via Sol–gel Process and Its Photocatalytic Activity for Degradation of Methyl Orange

Photocatalytic Activity of Defective TiO2-x for Water Treatment/Methyl Orange Dye Degradation

TiO2 Nanoparticles Supported on PMMA Nanofibers for Photocatalytic Degradation of Methyl Orange

Photocatalytic Degradation of Methyl Orange by TiO2-coated Activated Carbon and Kinetic Study.

Microorganism-Templated Nanoarchitectonics of Hollow TiO2-SiO2 Microspheres with Enhanced Photocatalytic Activity for Degradation of Methyl Orange

Photocatalytic degradation of methyl orange in aqueous suspension of mesoporous titania nanoparticles

Photocatalytic Degradation of Methyl Orange over Y3+ Doped TiO2 Pillared Montmorillonite

Morphology-dependent photocatalytic activity of TiO<sub>2</sub> crystals

Study on relationship of particle structure and photocatalytic properties of nano-TiO2 powder

Studies on the Relationship Between the Crystal Form of Tio2 and Its Photocatalyzing Degradation Efficiency

Preparation of Controllable Crystalline Titania and Study on the Photocatalytic Properties.

Preparation and Photocatalytic Performance of TiO2 Thin Films

Degradation of Methyl Orange by V5+ ,ag+ Co-doped Nano-TiO2

Mechanisms of Enhancement Photocatalytic Properties and Activity Nd3+-Doped Tio2 for Methyl Orange Degradation

Enhanced Photocatalytic Activity of (mo, C)-Codoped Anatase Tio2 Nanoparticles for Degradation of Methyl Orange under Simulated Solar Irradiation