Abstract:Morphology and crystalline-phase control of titanium dioxide is a crucial issue in the study of photocatalytic activity. Here, we present a facile synthetic path combing the solgel method with solvothermal treatment to form hybrid mesoporous and microporous TiO2. The TiO2 precursor was obtained by the solgel method, and this was self-assembled into mesopores and micropores by NH4F corrosiveness on the surface of TiO2 under hydrothermal conditions. Powder X-ray diffraction (XRD), thermogravimetric analysis and differential scanning calorimetry (TGA/DSC), X-ray photoelectron spectroscopy (XPS), N-2 adsorption measurements, transmission electron microscopy (TEM) and Raman spectroscopy were used to characterise the titania powders. The results reveal that NH4F not only improved the formation of the crystallised anatase phase but also served as a corrosive agent modified on the surface of TiO2 precursors. Defective voids among these nanoparticles formed micropores by hydrothermal reaction of NH4F and TiO2 over a long time. When the NH4F concentration was 1.0 mol.L-1, micropores became dominant,and few mesopores were obtained, and this results in a smaller average pore size. Thus, mesoporous and microporous structures were formed. Furthermore, these crystallised mesoporous and microporous anatase titania nanoparticles with uniform structure and high surface area have a higher photocatalytic activity for azo dye degradation under near UV irradiation.

Synthesis of Controllable Crystalline Nano-Tio2 at Low Temperature

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Preparation of Controllable Crystalline Titania and Study on the Photocatalytic Properties.

Low-Temperature Synthesis of Flower-Like Tio2 Nanocrystals

Low-Temperature Synthesis of Nanostructured TiO2 Particles and Their Photocatalytic Oxidation Activity

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Synthesis and photocatalytic properties of nano bi-crystalline titania of anatase and brookite by hydrolyzing TiOCl2 aqueous solution at low temperatures

Synthesis of Nano-TiO2 with Anatase Structure at Low Temperature

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

UV/ozone-assisted Low Temperature Preparation of Mesoporous TiO2with Tunable Phase Composition and Enhanced Solar Light Photocatalytic Activity

Facile and large-scale synthesis of hollow TiO2 nanostructures from TiCl3 solution

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Synthesis of Nanocrystal Titania Sol with Different Ratio of Rutile and Anatase at Low Temperature

Various Tio2 Microcrystals: Controlled Synthesis and Enhanced Photocatalytic Activities

Microemulsion-mediated solvothermal synthesis and photocatalytic properties of crystalline titania with controllable phases of anatase and rutile.

Crystallinity Control on Photocatalysis and Photoluminescence of TiO2-based Nanoparticles

Controlled Synthesis of Titanium Dioxide Nanostructures

Synthesis and Characterization of TiO_2 Nano-crystalline with Different Morphologies by Low-temperature Hydrothermal Method