Abstract:In order to study the durability of concrete materials subjected to sulfate attack, in a sulfate attack environment, a series of concrete tests considering different fly ash contents and erosion times were conducted. The mechanical properties and the micro-structure of concrete under sulfate attack were studied based on the following: uniaxial compressive strength test, split tensile test, ultrasonic impulse method, scanning electron microscopy (SEM) and X-ray diffraction (XRD). The mechanical properties were compressive strength, splitting tensile strength, and relative dynamic elastic modulus, respectively. Additionally, according to the damage mechanical theory, experimental results and micro-structure analysis, the damage evolution process of concrete under a sulfate attack environment were studied in detail. Finally, according to the sulfate attack time and fly ash content, a damage model of the sulfate attack of the binary surface was established. The specific results are as follows: under the action of sulfate attack, the change law of the rate of mass change, relative dynamic modulus of elasticity, corrosion resistance coefficient of compressive strength, and the corrosion resistance coefficient of the splitting tensile strength of concrete all increase first and then decrease. Under the same erosion time, concrete mixed with 10% fly ash content has the best sulfate resistance. Through data regression, the damage evolution equation of the sulfate attack was developed and there is an exponential function relationship among the different damage variables. The binary curved surface regression effect of the concrete damage and the erosion time and the amount of fly ash is significant, which can predict deterioration of concrete damage under sulfate attack. During the erosion time, the combined expansion of ettringite and gypsum caused micro cracks. With an increase of corrosion time, micro cracks developed and their numbers increased.

Experimental and Numerical Study of the Effects of Solution Concentration and Temperature on Concrete under External Sulfate Attack

A Chemical-Transport-Mechanics Numerical Model for Concrete under Sulfate Attack

A chemo-transport-damage model for concrete under external sulfate attack

Numerical Investigation of External Sulfate Attack and Its Effect on Chloride Binding and Diffusion in Concrete

Deformation behaviour of concrete materials under the sulfate attack

Numerical Study on the Chemical and Electrochemical Coupling Mechanisms for Concrete under Combined Chloride-Sulfate Attack

A chemo-thermo-damage-transport model for concrete subjected to combined chloride-sulfate attack considering the effect of calcium leaching

Effect of Multiple Ions on the Degradation in Concrete Subjected to Sulfate Attack

A chemo-mechanical coupling model for concrete lining subjected to external sulfate attack

Mesoscale modeling and simulation on the chemo-mechanical behavior of concrete in sulfate-rich environments

Numerical simulation of external sulphate attack in concrete considering coupled chemo-diffusion-mechanical effect

Numerical Modeling Of The Effect Of Concrete Porosity Evolution On Electrochemical Chloride Removal From Concrete Structures

A multi-phase numerical simulation method for the changing process of expansion products on concrete under sulfate attack

Experimental investigation on the fracture properties of concrete under different exposure conditions

RESEARCH ON MECHANISM OF SULFATE ATTACK ON CONCRETE BY TG-DSC METHOD

Mechanical Properties and Damage Evolution of Concrete Materials Considering Sulfate Attack

Reliability assessment of concrete under external sulfate attack

Mesoscale numerical simulation on the deterioration of cement-based materials under external sulfate attack

Experimental Investigation on the Effect of Sulfate Attack on Chloride Diffusivity of Cracked Concrete Subjected to Composite Solution

Chemo-mechanical modelling of the external sulfate attack in concrete

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete