Abstract:The diffusion of chloride ions in reinforced concrete under the seawater environment will affect the physical or mechanical properties and durability. Sulfate ions also influence the diffusion of chloride ions by generating expansion products through physical and chemical reactions. Further research on the effects of chloride binding and sulfate ion attack on chloride ion diffusion will deepen the understanding of concrete failure mechanism. In this paper, a quaternary blend based on calcium sulfoaluminate (CSA) cement was prepared and laboratory immersion tests were conducted in artificial seawater with varying salt concentrations. Initially, chloride ion concentration measurements and XRD tests were conducted at different corrosion ages and salt concentrations. Subsequently, the chloride binding properties of CSA-based materials was quantified through the analysis of chloride ion concentration and the phases of hydration products. Meanwhile, the corrosive effect of sulfate ions on chloride ion diffusion was determined corresponds to the content of expansive hydration products. Furthermore, numerical simulations were employed to evaluate the impact of sulfate ion corrosion, chloride binding, and their combined effects on chloride ion diffusion, and the results were compared with free chloride ion concentration ( C f ). The results indicate that the total chloride ion concentration ( C t ) exhibits a linear relationship with increasing salt concentrations of seawater in CSA-based materials. Meanwhile, the bound chloride ion concentration ( C b ) follows a logarithmic growth pattern. The chloride binding rate experiences a linear decline with the increase of chloride ion concentration in the artificial seawater. Additionally, the relationship between C f and C b or C t can be described using different isothermal adsorption models for the CSA-based materials. Among these models, the Langmuir model is suitable for characterizing the relationship between C f and C b , while the Freundlich model is suitable for describing the relationship between C f and C t . Furthermore, it is noteworthy that sulfate ion attack and chloride binding exert nearly equivalent effects on the diffusion of chloride ions in CSA-based materials at short corrosion age and low chloride ion concentration. However, the corrosive impact of sulfate ions gradually evolves into the dominant factor in the progression of corrosion over time and the increase in seawater salt concentration.

Experimental Investigation on the Effect of Sulfate Attack on Chloride Diffusivity of Cracked Concrete Subjected to Composite Solution

Study On Relationship Between Chloride Diffusion In Concrete And Time

Theoretical and Experimental Investigation of Loading Effects on Chloride Diffusion in Saturated Concrete

InfIuence of Ioad crack on chIoride diffusion in concrete

Experimental Study on Chloride Ion Transport in Concrete Structure under Shear Stress

Interaction Effect of Chloride Attack and Carbonization in Concrete

Modeling of chloride ions diffusion in cracked concrete

Effect of Sulfate Concentration on Chloride Diffusion of Concrete under Cyclic Load

A Numerical Study on Chloride Diffusion in Freeze-Thaw Affected Concrete

Experimental investigation on the fracture properties of concrete under different exposure conditions

Experimental and Numerical Study on the Microstructure and Chloride Ion Transport Behavior of Concrete-to-concrete Interface

Effect of chloride binding and sulfate ion attack on the chloride diffusion in calcium sulfoaluminate-based material under seawater environment

Finite element analysis on the diffusion-reaction-damage behavior in concrete subjected to sodium sulfate attack

Study on the mechanism and numerical modeling of chloride ingress in cracked concrete

A Numerical Study on Chloride Migration in Cracked Concrete Using Multi-Component Ionic Transport Models

Influence of Stochastic Cracks on Sulfate Diffusion in Concrete of Underground Structure

Influence of the coupled effect of stray current and sulfate upon chloride diffusing into concrete of underground structures

Study on Concrete Deterioration in Different NaCl-Na2SO4 Solutions and the Mechanism of Cl- Diffusion

Influence of cracking on chloride diffusivity and moisture influential depth in concrete subjected to simulated environmental conditions

Model of Chloride Penetration into Cracked Concrete Subject to Drying–wetting Cycles

Chloride ingression in cracked concrete under saturated state