Abstract:Due to the non-uniform distribution of meso-structure, the diffusion of chloride ions in concrete show the characteristics of characteristics of randomness and fuzziness, which leads to the non-uniform distribution of chloride ions and the non-uniform corrosion of steel rebar in concrete. This phenomenon is supposed as the main reason causing the uncertainty of the bearing capacity deterioration of reinforced concrete structures. In order to analyze and predict the durability of reinforced concrete structures under chloride environment, the random features of chloride ions transport in concrete were studied in this research from in situ meso-structure of concrete. Based on X-ray CT technology, the spatial distribution of coarse aggregates and pores were recognized and extracted from a cylinder concrete specimen. In considering the influence of ITZ, the in situ meso-structure of concrete specimen was reconstructed to conduct a numerical simulation on the diffusion of chloride ions in concrete, which was verified through electronic microprobe technology. Then a stochastic study was performed to investigate the distribution of chloride ions concentration in space and time. The research indicates that the influence of coarse aggregate on chloride ions diffusion is the synthetic action of tortuosity and ITZ effect. The spatial distribution of coarse aggregates and pores is the main reason leading to the non-uniform distribution of chloride ions both in spatial and time scale. The chloride ions concentration under a certain time and the time under a certain concentration both satisfy the Lognormal distribution, which are accepted by Kolmogorov-Smirnov test and Chi-square test. This research provides an efficient method for obtain mass stochastic data from limited but representative samples, which lays a solid foundation for the investigation on the service properties of reinforced concrete structures.

Influence of Stochastic Cracks on Sulfate Diffusion in Concrete of Underground Structure

Stochastic investigation on three-dimensional diffusion of chloride ions in concrete

Modeling of chloride ions diffusion in cracked concrete

InfIuence of Ioad crack on chIoride diffusion in concrete

Experimental Investigation on the Effect of Sulfate Attack on Chloride Diffusivity of Cracked Concrete Subjected to Composite Solution

Effect of Micro-Cracks on Chloride Ion Diffusion in Concrete Based on Stochastic Aggregate Approach

Transient diffusion behavior of chloride ions in concrete with a macro crack

Finite element analysis on the diffusion-reaction-damage behavior in concrete subjected to sodium sulfate attack

Statistic Investigation on Chloride Ions Distribution Based on Numerical Reconstruction of in Situ Meso-Structure of Concrete

Study on the mechanism and numerical modeling of chloride ingress in cracked concrete

Chloride ingression in cracked concrete under saturated state

Modelling the corrosion mechanism of steel bars in chloride-contaminated concrete with transverse cracks

Theoretical and Experimental Investigation of Loading Effects on Chloride Diffusion in Saturated Concrete

FRACTAL ANALYSIS OF STRESS-DEPENDENT DIFFUSIVITY OF POROUS CEMENTITIOUS MATERIALS

Crack shape and rust distribution in corrosion-induced cracking concrete coupled with load

Assessment of two-dimensional diffusions of sulfate ions in concrete based on one-dimensional condition

Influence of cracking on chloride diffusivity and moisture influential depth in concrete subjected to simulated environmental conditions

A Numerical Study on Chloride Migration in Cracked Concrete Using Multi-Component Ionic Transport Models

Model of Chloride Penetration into Cracked Concrete Subject to Drying–wetting Cycles

Diffusion model of sulfate ions in concrete based on pore change of cement mortar and its application in mesoscopic numerical simulation

Multi-scale model investigating the effects of pore structure and drying-wetting cycles on diffusion in concrete