Abstract:In order to study the durability of concrete materials subjected to sulfate attack, in a sulfate attack environment, a series of concrete tests considering different fly ash contents and erosion times were conducted. The mechanical properties and the micro-structure of concrete under sulfate attack were studied based on the following: uniaxial compressive strength test, split tensile test, ultrasonic impulse method, scanning electron microscopy (SEM) and X-ray diffraction (XRD). The mechanical properties were compressive strength, splitting tensile strength, and relative dynamic elastic modulus, respectively. Additionally, according to the damage mechanical theory, experimental results and micro-structure analysis, the damage evolution process of concrete under a sulfate attack environment were studied in detail. Finally, according to the sulfate attack time and fly ash content, a damage model of the sulfate attack of the binary surface was established. The specific results are as follows: under the action of sulfate attack, the change law of the rate of mass change, relative dynamic modulus of elasticity, corrosion resistance coefficient of compressive strength, and the corrosion resistance coefficient of the splitting tensile strength of concrete all increase first and then decrease. Under the same erosion time, concrete mixed with 10% fly ash content has the best sulfate resistance. Through data regression, the damage evolution equation of the sulfate attack was developed and there is an exponential function relationship among the different damage variables. The binary curved surface regression effect of the concrete damage and the erosion time and the amount of fly ash is significant, which can predict deterioration of concrete damage under sulfate attack. During the erosion time, the combined expansion of ettringite and gypsum caused micro cracks. With an increase of corrosion time, micro cracks developed and their numbers increased.

Deformation behaviour of concrete materials under the sulfate attack

An Internal Expansive Stress Model of Concrete under Sulfate Attack

A Chemical-Transport-Mechanics Numerical Model for Concrete under Sulfate Attack

Reliability assessment of concrete under external sulfate attack

Study on the expansion of concrete under attack of sulfate and sulfate–chloride ions

A Micromechanical-Based Semi-Empirical Model for Predicting the Compressive Strength Degradation of Concrete under External Sulfate Attack

A time–space porosity computational model for concrete under sulfate attack

Mechanical Properties and Damage Evolution of Concrete Materials Considering Sulfate Attack

A Time-Space Porosity Model Based on the Volume Expansion of Chemical Products of Concrete Under Sulfate Attack

Finite element analysis on the diffusion-reaction-damage behavior in concrete subjected to sodium sulfate attack

A failure thickness prediction model for concrete exposed to external sulfate attack

A chemo-transport-damage model for concrete under external sulfate attack

Damage Constitutive Model and Mechanical Performance Deterioration of Concrete under Sulfate Environment

Experimental study on underground structure concrete under static bending loads and sulfate attack

A multi-phase numerical simulation method for the changing process of expansion products on concrete under sulfate attack

Numerical simulation of external sulphate attack in concrete considering coupled chemo-diffusion-mechanical effect

Damage Mechanism of Concrete Deteriorated by Sulfate Attack in Wet-Dry Cycle Environment

Combined effects of sulfate attack under drying–wetting cycles and loading on the fatigue behavior of concrete

Theoretical and Experimental Investigation of Loading Effects on Chloride Diffusion in Saturated Concrete

A chemo-mechanical coupling model for concrete lining subjected to external sulfate attack