Abstract:An accurate evaluation of sulfate attack (SA) diffusion and damage processes is critical for durability design in sulfate-contaminated environments. This study presents a three-dimensional cellular automata model algorithm (3D-CAm) that effectively simulates sulfate diffusion processes in concrete. The model's efficacy was verified through comparison with analytical solutions of Fick's second law (FSL), experimental data, and numerical methods reported in the literature. The outcomes demonstrate that the model has a high degree of accuracy in simulating the diffusion processes of SA in concrete. Moreover, based on the diffusion characteristics of sulfate, damage evolution, and deterioration of concrete mechanical properties, the 3D-CAm is developed and applied for modeling and evaluating the long-term effects of SA on the durability of a concrete bridge. The time and space-dependent multifactorial diffusivity stochastic effects were considered. The model algorithms are developed in Python to achieve this purpose. The simulation results revealed that the randomness of the multifactorial had a negative effect on the increasing sulfate diffusion and accelerating the degradation of the mechanical properties of concrete. Moreover, the relationship between sulfate concentration, damage degree, and corrosion time is presented. The results indicate that the damage degree plays a critical role in the deterioration of the mechanical properties of concrete, where with the increase in service time, the mechanical properties show a noteworthy decrease due to the increase in corrosion depth and deterioration of the cross-section area. To conclude, the 3D-CAm model provides a suitable and effective method for evaluating the diffusion and damage processes of SA in concrete bridges. It offers a valuable way to evaluate damage risk and design durable projects in corrosive environments.

Mesoscale modeling and simulation on the chemo-mechanical behavior of concrete in sulfate-rich environments

Mesoscale numerical simulation on the deterioration of cement-based materials under external sulfate attack

A Chemical-Transport-Mechanics Numerical Model for Concrete under Sulfate Attack

A chemo-micromechanical damage model of concrete under sulfate attack

Chemo-mechanical modelling of the external sulfate attack in concrete

A chemo-mechanical coupling model for concrete lining subjected to external sulfate attack

3 D In-situ XCT Image Based Mesoscale Fracture Modelling and Validation of Concrete Using Voxel Hexahedron Meshing and Damage Plasticity Model

A Micromechanical-Based Semi-Empirical Model for Predicting the Compressive Strength Degradation of Concrete under External Sulfate Attack

A multi-phase numerical simulation method for the changing process of expansion products on concrete under sulfate attack

A time–space porosity computational model for concrete under sulfate attack

Numerical simulation of external sulphate attack in concrete considering coupled chemo-diffusion-mechanical effect

A Mesoscale Modelling Approach Coupling SBFEM, Continuous Damage Phase-Field Model and Discrete Cohesive Crack Model for Concrete Fracture

A Time-Space Porosity Model Based on the Volume Expansion of Chemical Products of Concrete Under Sulfate Attack

Three-phase Modelling of Electrochemical Chloride Removal from Corroded Steel-Reinforced Concrete

Multi-phase Modelling of Electrochemical Rehabilitation for ASR and Chloride Affected Concrete Composites

A chemo-transport-damage model for concrete under external sulfate attack

A 3D multi-phase meso-scale model for modelling coupling of damage and transport properties in concrete

A Mesoscale Three-Dimensional Moisture Transport Model in Concrete

Damage Constitutive Model and Mechanical Performance Deterioration of Concrete under Sulfate Environment

Numerical simulation on the crystallization-induced mechanical response in hardened cement paste under external sulfate attack

An approach for simulating and evaluating the effect of sulfate attack on the durability of concrete bridges based on a three-dimensional cellular automata model