Abstract:In this paper, the NO-SCO (the selective catalytic oxidation of NO) experiments of single-phase Mn2O3, supported Mn2O3/Al2O3, and the Ce-doped MnxCey/Al catalyst system were carried out. The physical and chemical properties of the catalysts were analyzed by XRD, BET, XPS, SEM, O2-TPD, and H2-TPR. The effects of loading and Ce doping on catalyst activity were studied. The results show that the Mn2O3 catalyst exhibited the best activity at 300 ℃, and the NO conversion rate of Mn2O3 was 78.2%. The relative content of Oα adsorbed on the surface of the Mnx/Al catalyst decreased obviously by loading Mn2O3 on γ-Al2O3, which led to the decrease in catalyst activity. And the temperature window moved to the high-temperature region. After doping Ce, the dispersion of Mn enhanced, and the relative content of oxygen Oα adsorbed on the surface increased. The low-temperature activity and fluidity of oxygen in catalysts were improved. Among them, the Mn0.2Ce0.08/Al catalyst obtained a high specific surface area, good pore structure, large oxygen storage capacity, and excellent surface oxygen species. The corresponding NO conversion rate reached 83.5% at 290 ℃. Then, the effects of operating parameters such as space velocity, NO concentration, and O2 content on the catalytic activity of Mn0.2Ce0.08/Al were discussed. The experimental results show that the NO conversion rate of Mn0.2Ce0.08/Al decreased with increasing NO concentration and space velocity. The O2 content had a positive effect on the catalytic activity of the catalyst. However, the NO conversion rate tended to be stable due to the saturation of oxygen adsorbed on the catalyst. Through cycling experiments, we found that Mn2O3, Mn0.2/Al, and Mn0.2Ce0.08/Al catalysts showed good oxidation stabilities for NO oxidation. The evaluation of the water and sulfur resistance of the catalyst shows that the toxicity of SO2 was reduced by the aqueous atmosphere to a certain extent. Through the structural optimization of the basic model and the calculation of the NO-SCO reaction path, the results show that the NO-SCO reaction on the Mn2O3 (110) face followed the ER mechanism more. For the Mn2O3/Al2O3 (110) surface, the LH-MvK hybrid mechanism can greatly reduce the desorption energy barrier of the reaction intermediates, which is more favorable for the NO-SCO reaction. The catalytic mechanisms of the MnxCey/Al catalysts require further in-depth research.

The Synergy Between Manganese Oxide and Iron Oxide in NO Catalytic Removal with MnFeOx/SiO2 Catalyst

New Insights into the Relationships Between Performance and Physicochemical Properties of FeOx–NbOx Mixed Oxide Catalysts for the NH3-SCR Reactions

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Mnox/Ceo2/Sio2 Catalysts Prepared by Adsorption Phase Reaction Technique for Selective Catalytic Reduction of Nox at Low-Temperature

Surface Tailoring on Bifunctional CuOx/MnO2 Catalyst to Promote the Selective Catalytic Reduction of NO with NH3 and Oxidation of CO with O2

Mn-Modified CuO, CuFe2O4, and Γ-Fe2o3 Three-Phase Strong Synergistic Coexistence Catalyst System for NO Reduction by CO with a Wider Active Window.

Low-Temperature Selective Catalytic Reduction of NOx with NH3 over Fe–Mn Mixed-Oxide Catalysts Containing Fe3Mn3O8 Phase

Highly dispersed MnOx-FeO(x)supported by silicalite-1 for the selective catalytic reduction of NO(x)with NH(3)at low temperatures

Improvement of sulfur and water resistance with Fe-modified S-MnCoCe/Ti/Si catalyst for low-temperature selective catalytic reduction of NO with NH3

Unraveling the synergy between MnOx and CeO2 in MnOx-CeO2 SCR catalysts based on experimental and DFT studies

Interactions between CO oxidation and selective catalytic reduction of NO with NH3 over Mn-based catalysts

Promotional effect of iron oxide on the catalytic properties of Fe–MnOx/TiO2 (anatase) catalysts for the SCR reaction at low temperatures

Selective catalytic reduction of NO with NH3 over MnOx-CeO2 catalysts: The great synergy between CeO2 and crystalline phase of Mn3O4

Comparative analysis the dual origins of N2O byproduct on MnOx, FeOx and MnFeOx sphere catalysts for low-temperature SCR of NO with NH3

Synthesis of Mn-Fe/γ-Al2O3 and Its Performance in Catalytic Oxidation of NO

Effects of SiO2 Addition on SCR Performance of TiO2 Supported Manganese-Cerium Catalysts

A Novel MnOx–MoOx Codoped Iron-Based Catalyst for NH3-SCR with Superior Catalytic Activity over a Wide Temperature Range

Supported Mn2O3-based Catalysts for NO-SCO: an Experimental Study

The facilitating effect of sulfide treatment coupled sol-gel method on NH 3 -SCR activity of Fe–Mn/TiO 2 catalysts

Understanding the high performance of an iron-antimony binary metal oxide catalyst in selective catalytic reduction of nitric oxide with ammonia and its tolerance of water/sulfur dioxide

Dual Effect of Sulfation on the Selective Catalytic Reduction of NO with NH3 over MnOx/TiO2: Key Factor of NH3 Distribution