Enhanced Dielectric Properties of La-doped 0.75Batio3-0.25Bi(mg0.5ti0.5)o3 Ceramics for X9R-MLCC Application

Weijun Zhang,Jinlun Yang,Fenglin Wang,Xingyu Chen,Haijun Mao

DOI: https://doi.org/10.1016/j.ceramint.2020.10.009

IF: 5.532

2020-01-01

Ceramics International

Abstract:A series of 0.75Ba((1-x))La(2x/3)TiO(3)-0.25Bi(Mg0.5Ti0.5)O-3 (x = 0-0.2) ceramics have been synthesized by doping La2O3 into 0.75BaTiO(3)-0.25Bi(Mg0.5Ti0.5)O-3 (0.75BT-0.25BMT), and their structure and dielectric properties investigated. Upon characterizing the structural properties, the single-phase perovskite structure is identified for all the samples and the long-range order of 0.75BT-0.25BMT is verified to be further destroyed with the addition of La2O3. Moreover, it is found that the density of 0.75BT-0.25BMT can be improved by doping with La2O3, which also promotes the grain growth. Regarding the dielectric properties, the peak shifting effect induced by La3+ improves the permittivity-temperature stability of 0.75BT-0.25BMT remarkably by strengthening its relaxation behavior. Among all the samples, 0.75Ba(0.8)La(0.4/3)TiO(3)-0.25Bi(Mg0.5Ti0.5)O(3)( )shows the most outstanding permittivity-temperature stability with epsilon(r) = 572 +/- 15% (compared with epsilon(r) at 25 degrees C) over the temperature range -70 degrees C-238 degrees C at 1 kHz, which is notably better than that of 0.75BT-0.25BMT (-4 degrees C-58 degrees C) and satisfies the specification of the X9R multilayer ceramic capacitor (MLCC). Our work provides one promising option for selecting an alternative dielectric material in terms of permittivity-temperature stability, which advances the development of the X9R MLCC.