Abstract:A tribo-oxide layer is generally formed on the contact surfaces during the high temperature friction and wear process, which significantly influences the tribological properties of the materials. In this work, the evolution mechanism of tribo-oxide layer for nickel-based superalloy was studied. High temperature sliding wear tests were performed at the different sliding time from 1 min to 60 min for nickel-based superalloy (Ni-16Cr-13Co-4Mo) against a Si3N4 ball at 800°C under ambient environment. Morphology and chemical composition of the worn surface and wear debris were investigated using a Scanning electron microscope (SEM), X-Ray diffraction (XRD) and Raman spectroscope. The cross-sectional microstructure and element distribution of the worn surface and untested area were characterized by EDS mapping attached to the SEM. Results show that the evolution of tribo-oxide layer can be divided into three stages. The first stage is characterized by the formation of a mixed oxide layer due to the preferential oxidation of Cr, Al and Ti in the preheating and temperature holding process. In the second stage, a dense tribo-oxide layer is formed by compacting and sintering the wear debris retained on the worn surface accompanying the inner oxidation of the dissolved γ' phase and Cr in the alloy. In the third stage, the oxide layer with a layered structure formed with an outmost layer composed of mixed oxides with a spinel structure and an inner oxide layer played a barrier role to prevent further oxidation of the substrate. It is speculated that the change in the structure of spinel oxides at high temperature from order to disorder led to the decrease in shear stress, eventually resulted in the reduction of friction coefficient and the low wear rate.

FRICTION AND WEAR OF AL(2)O(3)-NI COMPOSITE

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Effect of Ni content on the wear behavior of Al-Si-Cu-Mg-Ni/SiC particles composites

Investigation of Friction and Wear Behavior of NiAl-based Alloys at Room Temperature

Wear Properties of NiAl Based Materials

Investigation of the Friction Layer of Ni3al Matrix Composites

Dry sliding wear characteristics of in-situ hybrid (Al 3 Ni + Al 2 O 3 )–Al composites

Microstructure, Mechanical Properties and High Temperature Tribological Behavior of NiAl-based Composites

Friction and Wear Behavior of NiAl–10wt%Ti3SiC2 Composites

Effects of Ni-5 wt% Al/Bi2O3 addition and heat treatment on mechanical and tribological properties of atmospheric plasma sprayed Al2O3 coating

Friction and Wear Behaviors of Ni-based Composites Containing Graphite/Ag 2 MoO 4 Lubricants

Microstructure, Friction, And Wear Properties Of Ni-Al2o3-Mos2 Composite Coatings

Investigation on Microstructure and Wear Behavior of the NiAl–TiC–Al2O3 Composite Fabricated by Self-Propagation High-Temperature Synthesis with Extrusion

Microstructures, Mechanical Properties and Tribological Behaviors of NiAl-based Composite Coatings with Various Addition of Nb

The evolution mechanism of tribo-oxide layer during high temperature dry sliding wear for nickel-based superalloy

Tribological Behaviors of Ni 3 Al Intermetallics with MoO 3 Multilayer Ribbon Crystal Prepared by Spark Plasma Sintering

Tribological performance of Ti3SiC2 enhanced Ni3Al matrix composites

Dry Sliding Wear of Nanostructured Fe30Ni20Mn20Al30

Effects of Ni content on microstructure and wear behavior of Al–13Si–3Cu–1Mg-xNi-0.6Fe-0.6Mn alloys

Influence of Ni-addition on Mechanical, Tribological Properties and Oxidation Resistance of AlCrSiN Coatings

Friction and Wear Characteristics of Hot-Pressed NiCr–Mo/MoO 3 /ag Self-Lubrication Composites at Elevated Temperatures Up to 900 °C