Abstract:Low-k SiONC thin films with excellent thermal stabilities were deposited using plasma-assisted molecular layer deposition (PA-MLD) with a tetraisocyanatesilane (Si(NCO)4) precursor, N2plasma, and phloroglucinol (C6H3(OH)3). By adjusting the order of the N2plasma exposure steps within the PA-MLD process, we successfully developed a deposition technique that allows accurate control of thickness at the Ångström level via self-limiting reactions. The thicknesses of the thin films were measured through spectroscopic ellipsometry (SE). By tuning the N2plasma power, we facilitated the formation of -NH2sites for phloroglucinol adsorption, achieving a growth per cycle of 0.18 Å cycle-1with 300 W of N2plasma power. Consequently, the thickness of the films increased linearly with each additional cycle. Moreover, the organic linkers within the film formed stable bonds through surface reactions, resulting in a negligible decrease in thickness of approximately -11% even upon exposure to a high annealing temperature of 600 °C. This observation was confirmed by SE, distinguishing the as-prepared film from previously reported low-k films that fail to maintain their thickness under similar conditions. X-ray photoelectron spectroscopy (XPS) and current-voltage (I-V) and capacitance-voltage (C-V) measurement were conducted to evaluate the composition, insulating properties, and dielectric constant according to the deposition and annealing conditions. XPS results revealed that as the plasma power increased from 200 to 300 W, the C/Si ratio increased from 0.37 to 0.67, decreasing the dielectric constant from 3.46 to 3.12. Furthermore, there was no significant difference in the composition before and after annealing, and the hysteresis decreased from 0.58 to 0.19 V owing to defect healing, while maintaining the leakage current density, breakdown field, and dielectric constant. The low dielectric constant, accurate thickness control, and excellent thermal stability of this MLD SiONC thin film enable its application as an interlayer dielectric in back-end-of-line process.

Low-temperature SiON films deposited by plasma-enhanced atomic layer deposition method using activated silicon precursor

Preparation Of Low-K Nanoporous Sio2 Films By Plasma-Enhanced Chemical Vapor Deposition

Plasma enhanced atomic layer deposition of silicon nitride using magnetized very high frequency plasma

Growth characteristics and electrical properties of SiO2 thin films prepared using plasma-enhanced atomic layer deposition and chemical vapor deposition with an aminosilane precursor

Synthesis of low-k SiONC thin films by plasma-assisted molecular layer deposition with tetraisocyanatesilane and phloroglucinol

Silicon oxynitride thin films by plasma-enhanced atomic layer deposition using a hydrogen-free metal-organic silicon precursor and N 2 plasma

Thermal Atomic Layer Deposition of Silicon Carbonitride: A Density Functional Theory Study

Effect of reactive gases (NH3/N2) on silicon–nitride thin films deposited with diiodosilane (SiH2I2) precursors

Room-temperature deposition of low H-content SiNx/SiNxOy thin films using a specially designed PECVD system

Correlation of film density and wet etch rate in hydrofluoric acid of plasma enhanced atomic layer deposited silicon nitride

Plasma-enhanced atomic layer deposition of silicon dioxide films using plasma-activated triisopropylsilane as a precursor

Remote Plasma Atomic Layer Deposition of SiNx Using Cyclosilazane and H2/N2 Plasma

Deposition and Thermoelectric Properties of N-Doped SiC Thick Films

Improving the structural performance of low-temperature sputtered AlN on silicon substrate

Characteristics of Nickel Thin Film and Formation of Nickel Silicide by Remote Plasma Atomic Layer Deposition using Ni(iPr-DAD)2

Low-temperature Synthesis of AlN Films Through Electron Cyclotron Resonance Plasma-Aided Reactive Pulsed Laser Deposition

RF Reactive Sputtering AlN Thin Film at Room Temperature for CMOS-compatible MEMS Application

Stability of SiNx Prepared by Plasma-Enhanced Chemical Vapor Deposition at Low Temperature

Low-Temperature Deposition of High-Quality SiO2 Films with a Sloped Sidewall Profile for Vertical Step Coverage

Plasma-enhanced atomic layer deposition of silicon nitride thin films with different substrate biasing using Diiodosilane precursor

Low-Temperature Deposition of AlN Films\+*