Impact of ZnO content in BAS glass–ceramics and pre‐oxidation temperature on Kovar alloys to their sealing strength
Han Jia,Cong Ao,Yue Mi,Tiesong Lin,Xiaofeng Zhang,Hong Li,Dehua Xiong
DOI: https://doi.org/10.1111/jace.20233
IF: 4.186
2024-10-25
Journal of the American Ceramic Society
Abstract:Graphical abstract: In this work, the coefficient of thermal expansion of B2O3–Al2O3–SiO2 (BAS) glass–ceramics increased from 48.17 to 54.92 × 10−7°C−1 with increasing of ZnO content. With an optimizing pre‐oxidized temperature of Kovar at 950°C, champion samples with the highest sealing strength of 6.08 MPa were achieved when BAS glass–ceramics sealed to Kovar at 1000°C for 30 min. Moreover, the sealing interface was observed to consist of four distinct regions: the Kovar alloy, the iron‐depleted Kovar, the iron‐rich zone, and the matrix glass–ceramics. This work studied the effect of Si/Zn ratio on the structure of B2O3–Al2O3–SiO2 (BAS) parent glass and the microstructure, properties of the resulting glass‐ceramics after heat treatment. Additionally, the effects of different pre‐oxidation temperature of Kovar alloys and sealing temperature on the shear strength of these sealed glass–ceramics‐to‐Kovar samples were studied. First, the parent glass precipitated three kinds of crystals Al0.52Zr0.48O1.74 (PDF#53‐0294), ZrO2 (PDF#37‐1484), and ZnAl2O4 (PDF#05‐0669) in BAS glass–ceramics. The coefficient of thermal expansion of glass–ceramics increased from 48.17 × 10−7 to 54.92 × 10−7°C−1 with the gradual increase of ZnO content. With an optimizing pre‐oxidized temperature of Kovar at 950°C, a champion sample with the highest sealing strength of 6.086 MPa was achieved when BAS glass–ceramics sealed to Kovar at 1000°C for 30 min. Moreover, the sealing interface was observed to consist of four distinct regions: the matrix alloy, the alloy iron‐deficiency area, the iron‐rich glass–ceramics, and the matrix glass–ceramics.
materials science, ceramics