Effect of microalloying with rare-earth lanthanum on dynamic recrystallization behavior and mechanical properties of Ti sheets
Yuanyuan Zhu,Yechen Deng,Yixin An,Kaige Wang,Ruoyu Liu,Lanyi Liu,Ziqi Wang,Yangzhihong Xiao,Bingfeng Wang
DOI: https://doi.org/10.1016/j.mtcomm.2024.109155
IF: 3.8
2024-05-13
Materials Today Communications
Abstract:This study examines the influence of microalloying with rare earth lanthanum (La) on the dynamic recrystallization behavior and mechanical properties of Titanium (Ti) sheets. A distinctive wedge-shaped specimen was employed for experimental efficiency, enabling continuous gradient strains to be applied to the Ti-La alloy during hot-rolling, facilitating the assessment of changing microstructural, textural, and hardness features as strain increased from low to high levels. The hot-rolled plates were performed using analytical methods such as optical microscopy (OM), X-ray diffraction (XRD), transmission electron microscopy (TEM), and hardness testing. The results show that the hardening process can be divided into four stages under continuous gradient strain (0 Ōł╝ 0.5, 0.5 Ōł╝ 0.7, 0.7 Ōł╝ 1.2 and 1.2 Ōł╝ 1.6). During these stages, grain refinement and dislocation strengthening emerge as critical contributors to changes in hardness. Furthermore, it was determined that dynamic recrystallisation (DRX) of Ti-La alloys during hot rolling occurs at the fourth stage. Analysis of the orientation distribution function (ODF) reveals that the dominant textures during this process include { 1╠ģ21╠ģ0 }, { 011╠ģ0 }, and { 0001 } textures. When compared with commercially pure titanium (CP-Ti), the Ti-La alloy shows significantly delayed DRX under identical conditions. The DRX grain growth appears suppressed, attributable to the presence of La-rich particles on the grain boundaries. Moreover, the texture associated with rolling deformation seems subdued, providing a desirable base for future cold rolling and heat treatment.
materials science, multidisciplinary