Abstract:High porosity (40% to 60%) 316L stainless steel containing well-interconnected open-cell porous structures with pore openness index of 0.87 to 1 were successfully fabricated by binder jetting and subsequent sintering processes coupled with a powder space holder technique. Mono-sized (30 μm) and 30% (by volume) spherically shaped poly(methyl methacrylate) (PMMA) powder was used as the space holder material. The effects of processing conditions such as: (1) binder saturation rates (55%, 100% and 150%), and (2) isothermal sintering temperatures (1000 ○C to 1200 ○C) on the porosity of 316L stainless steel parts were studied. By varying the processing conditions, porosity of 40% to 45% were achieved. To further increase the porosity values of 316L stainless steel parts, 30 vol. % (or 6 wt. %) of PMMA space holder particles were added to the 3D printing feedstock and porosity values of 57% to 61% were achieved. Mercury porosimetry results indicated pore sizes less than 40 μm for all the binder jetting processed 316L stainless steel parts. Anisotropy in linear shrinkage after the sintering process was observed for the SS316L parts with the largest linear shrinkage in the Z direction. The Young’s modulus and compression properties of 316L stainless steel parts decreased with increasing porosity and low Young’s modulus values in the range of 2 GPa to 29 GPa were able to be achieved. The parts fabricated by using pure 316L stainless steel feedstock sintered at 1200 ○C with porosity of ~40% exhibited the maximum overall compressive properties with 0.2% compressive yield strength of 52.7 MPa, ultimate compressive strength of 520 MPa, fracture strain of 36.4%, and energy absorption of 116.7 MJ/m3, respectively. The Young’s modulus and compression properties of the binder jetting processed 316L stainless steel parts were found to be on par with that of the conventionally processed porous 316L stainless steel parts and even surpassed those having similar porosities, and matched to that of the cancellous bone types.

Processing Research on Shaping Porous 316L Stainless Steel via SLS

Personalized Artificial Tibia Bone Structure Design and Processing Based on Laser Powder Bed Fusion

Optimization of Structural and Processing Parameters for Selective Laser Melting of Porous 316L Bone Scaffolds

Effect of scanning speed and laser power on formability, microstructure, and quality of 316L stainless steel prepared by selective laser melting

Finite Element Simulation of Stainless Steel Porous Scaffolds for Selective Laser Melting (SLM) and Its Experimental Investigation

Investigation into the effect of process parameters on density, surface roughness, and mechanical properties of 316L stainless steel fabricated by selective laser melting

The Process Research of 316L Stainless Steel in Selective Laser Melting

Effects of Process Parameters on the Microstructure and Properties of Selective Laser Melting 316L Negative Re-entrant Hexagonal Honeycomb Porous Bone Scaffolds

Investigation on the Attainment of High-Density 316L Stainless Steel with Selective Laser Sintering

Effect of porosity on compressive properties of porous sintered stainless steel fiber media

Influence of process parameters on the organization and properties of 316L-SCBCC bracket formed by selective zone laser melting

Simulation and experimental studies on process parameters, microstructure and mechanical properties of selective laser melting of stainless steel 316L

A comprehensive study of LPBF parameter influence in 316L stainless steel mechanical properties, macrostructure, and printability

Microstructure and properties of 316L stainless steel by selective laser melting under various process parameters

Investigation into the effect of process parameters on microstructural and physical properties of 316L stainless steel parts by selective laser melting

Study on performance optimization of 316L stainless steel parts by High-Efficiency Selective Laser Melting

Selective Laser Melting Bone-Compatible Pure Titanium Porous Structure

Fabrication and Mechanical Properties of Porous Cp-Tiusing Selective Laser Melting (Slm)

Binder Jetting Additive Manufacturing of High Porosity 316L Stainless Steel Metal Foams

316L Stainless Steel with Gradient Porosity Fabricated by Selective Laser Melting

Effect Of Powder Feedstock On Microstructure And Mechanical Properties Of The 316l Stainless Steel Fabricated By Selective Laser Melting