Abstract:In this study, {10-12} tensile twins (TTs) were induced in hot-rolled AZ31 Mg sheets via hot tension along the normal direction. The results demonstrate that the volume fraction of TTs at 2mm/min is greatly lower than their counterparts at 0.5mm/min at 100°C and 200°C. Dynamic recrystallization (DRX) can decrease twin nucleation rate during hot tensile when the strain rate reaches 2mm/min. Decrease in critical resolved shear stress of non-basal slips at 200°C enhances the deformation capability among grains, which dramatically reduces the volume fraction of TTs. Hence, TTs are hardly observed in 200°C-2mm/min sample. Tensile temperature significantly affects the morphology of TT lamellae. Grain boundaries prevents the longitudinal growth of the TTs, and then the thickness of TTs begins to grow to coordinate the deformation, resulting in fine TT lamellae in 100°C-0.5mm/min. Compared with AR, the basal texture intensity of 100°C-2mm/min and 200°C-2mm/min increases and the occurrence of DRX is the main reason, while basal texture weakening of 100°C-0.5mm/min and 200°C-0.5mm/min depends on the formation of TTs. Compared with samples at 200°C, the samples at 100°C have higher tensile stresses. The maximum stress of 100°C-0.5mm/min is 64.97 MPa when tensile strain reaches 0.15 owing to its highest dislocation density. 200°C-2mm/min possesses the highest hardness among the four tension samples, which is associated with the largest fraction of DRXed grains (68.8%) and its refinement strengthening effect. Dislocation strengthening exerts more influence on the hardness of 100°C-0.5mm/min.

Twinning and Dynamic Recrystallization in AZ31 Magnesium Alloy under Medium-High Strain Rate

Dynamic Recrystallization and Microstructure Evolution in AZ31 Magnesium Alloy During Thermomechanical Processing

Temperature and Strain Rate Dependence of Deformation Microstructures of Az31 Magnesium Alloy under Uniaxial Tension

Microstructure and Deformation Mechanism of AZ31 Magnesium Alloy under Dynamic Strain Rate

Twinning Effects on the Hot Deformation Behavior of AZ31 Mg Alloy

Plastic Deformation Mechanisms of AZ31 Magnesium Alloy under High Strain Rate Compression

Effect of Strain Rate on Dynamic Recrystallization in a Magnesium Alloy under Compression at High Temperature

Tensile Behavior and Microstructural Evolution for AZ31 Magnesium Alloys Sheet at High Strain Rate

Twinning, Dynamic Recrystallization, and Texture Evolution in As-Solution AZ80 Mg Alloy During Hot Compression

Quasi-in Situ Observation of Extension Twinning of AZ31 Magnesium Alloy under Co-Directional Dynamic Compression

Dynamic recrystallization and twinning behavior of magnesium alloy during hot tension

Effect of Pre-Existing {101¯2} Extension Twins on Mechanical Properties, Microstructure Evolution and Dynamic Recrystallization of AZ31 Mg Alloy During Uniaxial Compression

Asymmetry in the hot deformation behavior of AZ31B magnesium sheets

Deformation Behaviour and Dynamic Recrystallization of AZ61 Magnesium Alloy

Characteristics of Hot Tensile Deformation and Microstructure Evolution of Twin-Roll Cast AZ31B Magnesium Alloys

Initiation and Strain Compatibility of Connected Extension Twins in AZ31 Magnesium Alloy at High Temperature

Influence of strain rate on dynamic recrystallization behavior of AZ61 magnesium alloy

Influence of loading direction and strain rate on twinning of AZ31 magnesium alloy in plane-strain compression

Effect of Sample Orientation and Initial Microstructures on the Dynamic Recrystallization of a Magnesium Alloy

Role of {101‾2} Twinning in the Anisotropy and Asymmetry of AZ31 Magnesium Alloy under High Strain Rate Deformation

Microstructure evolution and characterization of the adiabatic shear bands in AZ31 magnesium alloy