Microstructure and Deformation Mechanism of AZ31 Magnesium Alloy under Dynamic Strain Rate

Chao Lou,Qi Sun,Qingshan Yang,Yi Ren,Zhengyuan Gao,Xiyan Zhang
DOI: https://doi.org/10.1007/s11665-018-3627-9
IF: 2.3
2018-01-01
Journal of Materials Engineering and Performance
Abstract:A hot-rolled AZ31Mg alloy sheet was subjected to dynamic plastic deformation parallel to the rolling direction, and microstructural evolutions and mechanical properties of the deformed samples were examined. It has been found that dynamic strain rate could facilitate {10-12} twin nucleation and growth and leads to a lower yield stress of about 20 MPa and an early end to twinning characteristic (happening at a strain point of about 6%) shown in the stress–strain curve. {10-12} twinning mechanism dominates the early plastic deformation; but when plastic strain exceeds ~ 9%, dislocation–slip mechanism instead of {10-12} twinning dominates the later plastic deformation. And this premature transformation of the dominant deformation mechanisms from {10-12} twinning to dislocation slip is caused by dynamic strain rate. The effect of dynamic strain rate on the number of twin nucleations remains unclear, and the more systematic researches are needed in the future.
What problem does this paper attempt to address?