Effect of Ε-Al3ni Phase on Mechanical Properties of Al–Si–Cu–Mg–Ni Alloys at Elevated Temperature

Lijie Zuo,Bing Ye,Jian Feng,Huixia Zhang,Xiangyang Kong,Haiyan Jiang

DOI: https://doi.org/10.1016/j.msea.2019.138794

IF: 6.044

2019-01-01

Materials Science and Engineering A

Abstract:The influence of epsilon-Al3Ni phase on tensile and creep performance of the Al-12Si-0.9Cu-0.8 Mg-(1-4)Ni alloys was investigated at elevated temperature. The Image-Pro Plus was used to characterize the volume fraction, mean particle size, and surface roundness of the epsilon-Al3Ni phase. The results show that the volume fraction of epsilon-Al3Ni phase is in accordance with the thermodynamic calculation and the mean particle size of epsilon-Al3Ni phase increases with Ni element. The ultimate tensile strength at 250 degrees C increases from 162 MPa to 187 MPa with the volume fraction of epsilon-Al3Ni phase varied from 1.03% to 8.20%. The elongation of the studied alloys shows a reverse trend. The minimum creep rates of the investigated alloys decrease with increasing the volume fraction of epsilon-Al3Ni phase. The decrease in minimum creep rate illustrates that the epsilon-Al3Ni phase is effective in improving the creep resistance of the Al-Si-Cu-Mg-Ni alloy.