Atomic-scale compositional complexity ductilizes eutectic phase towards creep-resistant Al-Ce alloys with improved fracture toughness
Meng Yi,Peng Zhang,Sihao Deng,Hang Xue,Chong Yang,Fuzhu Liu,Bin Chen,Shenghua Wu,Huaile Lu,Zhijian Tan,Jinyu Zhang,Yong Peng,Gang Liu,Lunhua He,Jun Sun
DOI: https://doi.org/10.1016/j.actamat.2024.120133
IF: 9.4
2024-06-27
Acta Materialia
Abstract:Hierarchical microstructures spanning from micro-sized eutectic structure to nano-sized precipitates are promisingly engineered in lightweight Al alloys to improve the high-temperature creep resistance that is increasingly required for rapid industrial development. However, the intrinsically-brittle eutectic phase is ready to fracture upon applied loading, which, dramatically reducing room-temperature ductility and fracture toughness, greatly hampers practical applications of the creep-resistant Al alloys. Here, through the combination of Sc microalloying with sub-rapid solidification, we observe the ductilization of Al 11 Ce 3 eutectic phase in cast heat-resistant Al-Ce-Sc alloys due to the formation of atomic-scale compositional complexity. High-concentration Sc atoms are frozen within the Al 11 Ce 3 intermetallic phase by the sub-rapid solidification, which then assemble into unusual atomic-scale compositional dipoles with the Sc atoms enriched at one pole and the Al atoms at the opposite during subsequent heat treatment. The dispersed Sc-Al compositional dipoles induce local lattice distortions that stimulate dislocation activities, as temporally and spatially visualized by in-situ neutron diffraction tensile test and microstructural characterizations. The unexpected plastic deformation triggered in Al 11 Ce 3 improves the deformation compatibility between the eutectic phases, enabling the sub-rapidly-solidified Al-Ce-Sc alloy to reach a room-temperature tensile elongation 3 times and fracture toughness over 8 times of its counterpart derived from traditional solidification. In addition, the sub-rapidly-solidified Al-Ce-Sc alloy exhibits an excellent creep resistance at 300 °C, achieving a tensile creep stress threshold of ∼ 70 MPa. These findings provide new perspectives on the design of ductile intermetallic phases and the development of creep-resistant Al alloys with application-level ductility.
materials science, multidisciplinary,metallurgy & metallurgical engineering