Abstract:The hot deformation behavior of TZM-1.0 wt% ZrO 2 alloy in the temperature range of 1000–1600 °C and strain rate range of 0.005–1 s −1 was studied by hot compression method. The constitutive equation and hot working diagram were established, and the microstructure evolution was emphatically analyzed by SEM and EBSD. The results indicate that the flow stress decreases with the increase of temperature and the decrease of strain rate, and ZrO 2 particles can improve the stability of TZM alloy in rate-control during hot deformation. The constitutive equation accurately predicted the correlation coefficient as high as 0.9685, calculated the average activation energy Q = 426 kJ mol −1 , and obtained the best process parameters of 1150 °C–1250 °C /0.01–0.05 s −1 under 0.7 strain. The unstable zone was mainly composed of a small number of coarse grains and a large number of fine grains. The main reason for flow instability was the disharmonious deformation between coarse and fine grains during compression. The optimum hot working zone consists of more uniform equiaxed grains. However, EBSD observed that at a strain rate of 1 s −1 , the recrystallization fraction at 1600 °C was lower than 1200 °C, and the dynamic recrystallization (DRX) and texture evolution trends at 1200 °C and 1600 °C were completely different. The abnormal changes in recrystallization fraction and texture evolution at 1600 °C were due to the competition between deformed grain growth and DRX on energy storage consumption, and the effect of deformed grain growth on energy storage consumption was greater than that of DRX. At 1600 °C/1 s −1 , the growth of deformed grains was dominant, exhibiting strong texture components in the [001] direction, with〈100〉fibers as the main component and the highest peak texture strength. As the strain rate decreases, DRX dominates and weakens the texture strength, resulting in a significant decrease in fibers.

Investigation on Compression Behavior of TZM and La 2 O 3 Doped TZM Alloys at High Temperature

High Temperature Mechanical Properties of TZM Alloys under Different Lanthanum Doping Treatments

Deformation behavior and microstructure evolution of TZM alloy with 1.0 wt%ZrO 2 under high temperature compression

Preparation and ductile-to-brittle transition temperature of the La-TZM alloy plates

Effect of La2 O3 on recrystallization temperature of TZM alloy

Microstructure and High Temperature Deformation Behavior of the Mo-ZrO 2 Alloys

Investigation of microstructure and tensile properties of as-processed TZM alloy at elevated temperature

Fracture and Microstructure of La Doped TZM Plate

Fracture behavior of the La-doped molybdenum-titanium-zirconium alloy

Microstructure Evolution of a Ti–Al–Sn–Zr Based Alloy During the Hot Compression Deformation

Investigation on the recrystallization and mechanical properties of a novel TZM alloy with heat treatment

La2O3 Effects on TZM Alloy Recovery, Recrystallization and Mechanical Properties

Evaluation of tensile property and strengthening mechanism of Zirconia reinforced molybdenum alloy

Effects of Rare Earth La Element Doping on Recrystallization Behavior of TZM Alloy Sheet

Hot Deformation Behavior and Microstructural Evolution of a TiB2/Al-Zn-Mg-Cu-Zr Composite

Effect of Strain Rate and Temperature on the Deformation Behavior in a Ti-23.1Nb-2.0Zr-1.0O Titanium Alloy

Effect of Temperature on Deformation Mechanisms of the Mg88Co5Y7 Alloy During Hot Compression

Hot Compressive Deformation Behavior And Microstructure Evolution Of Ti-6al-2zr-1mo-1valloy At 1073 K

Brittle-to-Ductile Transition and High-Temperature Deformation in ZrO<SUB>2</SUB>(Y<SUB>2</SUB>O<SUB>3</SUB>) and Al<SUB>2</SUB>O<SUB>3</SUB> Ceramics as Evaluated by Small Punch Test

Pt-plating effect on La-TZM alloy high temperature oxidation behavior

High Temperature Compressive Deformation Behavior of an Extruded Mg–8Gd–3Y–0.5Zr (wt.%) Alloy