Evaluating compressive property and hot deformation behavior of molybdenum alloy reinforced by nanoscale zirconia particles

Liujie Xu,Tielong Sun,Yucheng Zhou,Fangnao Xiao,Minjie Zhang,Shizhong Wei

DOI: https://doi.org/10.1016/j.jallcom.2020.158289

IF: 6.2

2021-04-01

Journal of Alloys and Compounds

Abstract:<p>The paper deals with the fabrication of molybdenum alloy bars with different ZrO₂ content via a series of processes, involving hydrothermal synthesis, co-precipitation, co-decomposition, powder metallurgy and rotary swaging. The compressive properties of molybdenum alloy bars were tested at various temperatures from room temperature to 1400 °C, and hot deformation behavior at different temperatures and strain rates was studied. The results show that ZrO₂ particles with the size of tens of nanometers are evenly dispersed in Mo matrix, and ZrO₂(110) and Mo(110) have a non-coherent interface due to a larger lattice misfit 13.57%. ZrO₂ particles could significantly reduce grain size of molybdenum alloy and improve its compressive properties. When the volume content of zirconia increases from 0 to 2.0%, the grain size of molybdenum alloys annealed at 1200 ℃ decreases sharply from 55.9 μm to 3.5 μm. The compressive yield strength (CYS) of Mo-2.0 vol%ZrO₂ annealed at 1200 °C is 674 MPa at room temperature, which is 65.6% higher than that of pure Mo. The high temperature CYS of Mo-2.0 vol% ZrO₂ at 1400 °C is 176 MPa, increasing 49.6% higher than that of pure Mo. Compared with the previous works, the peak flow stress of the new Mo-2.0 vol%ZrO₂ has been significantly improved. Adding of 2.0 vol%ZrO₂ increases the initial temperature of dynamic recrystallization to 1200°C, and effectively prevents the grain growth of dynamic recrystallization even at the increased deformation temperature of 1400 °C.</p>

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering