Deformation behaviors and the related high-temperature mechanical properties of Mg-11Gd-5Y-2Zn-0.7Zr via regulating extrusion temperatures
Jianxin Zhou,Hong Yang,Xiaojun Luo,Wenlong Xie,Bin Jiang,Zhihua Dong,Jiangfeng Song,Junyao Xu,Guangsheng Huang,Dingfei Zhang,Fusheng Pan
DOI: https://doi.org/10.1016/j.jmrt.2023.07.213
IF: 6.267
2023-08-02
Journal of Materials Research and Technology
Abstract:The effects of extrusion temperatures (430, 450, 470 and 490 °C) on the microstructures and mechanical properties of Mg-11Gd-5Y-2Zn-0.7Zr (GW) alloys at room temperature (RT), 250, 300, 350 °C were systematically investigated. The dynamic precipitation of blocky and lamellar long period stacking ordered (LPSO) phases was taken place during hot extrusion. The dominant texture changed from <10 1 ̄0 >//ED to //ED with increasing extrusion temperature. Tensile results indicated that the GW alloy extruded at 430 °C (GW430) exhibited the highest mechanical properties at both RT and elevated temperatures, which was ascribed to the fine dynamic recrystallized (DRXed) grains, un-DRXed grains with an orientation of <10 1 ̄0 >//ED, and the LPSO phase strengthening. When tensile tested below 300 °C, slips on the blocky LPSO phase and kinks of lamellar LPSO phase were the primary deformation modes, followed by grain boundary crack. At 350 °C, grain boundaries became the vulnerable sites to be activated. For GW alloys extruded at 450, 470 and 490 °C, an abnormal increase of mechanical properties was observed at 300 °C. This was due to the occurrence of multiple-slip, which showed the intersection and entanglement of dislocations and thus improving the strength of Mg matrix.
materials science, multidisciplinary,metallurgy & metallurgical engineering