Compressive Deformation of Polycrystalline Ni-Mn-Ga Alloys Near Chemical Ordering Transition Temperature

L. S. Wei,X. X. Zhang,M. F. Qian,P. G. Martin,L. Geng,T. B. Scott,H. X. Peng
DOI: https://doi.org/10.1016/j.matdes.2018.01.048
IF: 9.417
2018-01-01
Materials & Design
Abstract:Ferromagnetic shape memory Ni-Mn-Ga alloys exhibit an ordered L2(1) to partially ordered B2 transition at temperatures 873-1073 K. Based on the isothermal compressive results, it is demonstrated that L2(1) phase was brittle near ordering temperature, but the B2 phase was excellent above the chemical ordering temperature. In the compressive mode at temperatures of 473-1273 K and strain rates of 0.001-1 s(-1), the plastic deformation mechanism was found to be strongly dependent on the Zener-Hollomon parameter Z: the dynamic recrystallization was the dominant mechanism at the low Z region in the B2 state, then with increasing Z the dynamic recovery and ordering transition from B2 to L2(1) occurred, finally only dynamic recovery existed at the high Z region in the L2(1) state. Based on the processing map constructed from the isothermal compressive curves, hot extrusion of Ni-Mn-Ga alloy with ratio as high as 9:1 was achieved at 1273 K. This proved that polycrystalline Ni-Mn-Ga alloys are strikingly facile for large plastic deformation in the B2 state by dynamic recrystallization at temperatures around 1273 K and strain rate 0.03 s(-1), which affords a viable temperature and strain rate processing window for this intrinsically brittle alloy. (c) 2018 Elsevier Ltd. All rights reserved.
What problem does this paper attempt to address?