Abstract:Powder metallurgy (PM) α + β Ti-4Al-4Mo-4Sn-0.5Si alloys were fabricated through thermomechanical powder consolidation of TiH 2 -based powder compacts with two different processing routes: one involving blending the elemental powders (BE route) and the other involving mechanical milling a blend of elemental powders (MM route). With the MM + annealing + solution and aging (STA) route, a hierarchical microstructure consisting of necklace-like micron-scaled grain boundary α (α GB ) segments and isolated submicron-scaled primary α (α p ) rods dispersed in a β transformed structure (β t ) matrix containing a high number density of nano-scaled secondary α (α s ) laths was produced in the alloy. The alloy with the hierarchical microstructure achieved an excellent combination of a very high yield strength of 1339 MPa,an ultimate tensile strength of 1467 MPa and an excellent ductility of 10.4%. The increased strength was mainly due to the high fraction of β t matrix in which the fine-dispersed α s precipitates with different orientations efficiently blocked the dislocation motion during deformation. The excellent ductility achieved despite of the high flow stress can be attributed to the elimination of strain concentration in the α GB segments which prevented their cracking prior to the material reaching the necking point during plastic deformation. This was in contrast with the typical α/β t lamellar microstructure of the same alloy composition obtained with the BE + same heat treatment route where strain concentration in the α GB plates occurred due to the direct slip transmission from α colonies to adjacent parent α GB grains during plastic deformation, thus resulting in intergranular premature cracking. TEM observation demonstrated that the strain gradient from the α/β t interfaces to the domain interiors of both α GB segments and α p rods activated a high density of geometrically necessary dislocations near the interfaces, and caused an obvious synergistic strengthening effect which also contributed to the slow drop of strain hardening rate and thus was beneficial to improving the ductility.

Harmonically Structured Ti–6Al–4V Alloy with Ultrahigh Strength Fabricated by Thermomechanical Consolidation of Mechanically Milled TiH2/Al60V40 Powder Blend

Improving strain hardening capacity of high-strength Ti–6Al–4V alloy by a dual harmonic structure

The Role of Nanoscale Heterogeneous Structure in Simultaneously Enhancing Strength and Ductility of High-Oxygen Ti–6Al–4V Alloy

A novel Ti–6Al–4V alloy microstructure with very high strength and good ductility

Selective laser melting processing of heterostructured Ti6Al4V/FeCoNiCrMo alloy with superior strength and ductility

Ultrafine Composite Microstructure in a Bulk Ti Alloy for High Strength, Strain Hardening and Tensile Ductility

Hierarchical microstructure and strain partition of a PM α + β titanium alloy with an ultrahigh strength-ductility synergy

Strength enhancement of a bi-lamellar PM Ti–6Al–4V alloy without sacrificing ductility by Al partitioning and twinning-induced plasticity effect

Microstructure and Mechanical Properties of Ti-6Al-4V Rods Fabricated by Powder Compact Extrusion of TiH 2 /Al 60 V 40 Powder Blend

Ultrahigh Strength - Ductility in Ti-6Al-4V Composites with High-Activity Graphene-Induced In-Situ TiC and Coherent Nanophases

Making Titanium Alloys Ultrahigh Strength and Toughness Synergy Through Deformation Kinks-Mediated Hierarchical Α-Precipitation

Microstructure and Mechanical Properties of a High-Strength Ti-4Al-2Fe-3Cu Alloy Fabricated by Sintering and Hot Extrusion

A Novel Method to Produce Harmonic Structured Ti with Excellent Compressive Properties

Heterostructures Enhance Simultaneously Strength and Ductility of a Commercial Titanium Alloy

Making high primary α phase content titanium alloy exceptional strength and ductility by designing the heterogeneous structure

Achieving superior strength-ductility combination in the heterogeneous microstructured Ti64 alloy via multi-eutectoid elements alloying with CoCrFeNiMn during laser powder bed fusion

Investigating phase transformation, densification and diffusion mechanism of TiH 2 powder to achieve a high ductile Ti6Al4V alloy

Development of a Low-Density and High-Strength Titanium Alloy

Homogeneous α-precipitation and enhanced plasticity in Ti–6Cr–5Mo–5V–4Al high-strength metastable titanium alloy with heterogenous β-structure

Extraordinary tensile properties of titanium alloy with heterogeneous phase-distribution based on hetero-deformation induced hardening

Enhancing Strength-Ductility Synergy Via Hierarchical Microstructure in Fine-Grained Ti-10Mo-8V-1Fe-3.5Al Alloy