Abstract:A novel segmented control strategy for selenization environment is introduced to regulate the selenization reaction by controlling the evaporation area of Se. This selenization method helps to promote element homogenization, optimize surface smoothness, and obtain a high‐crystalline‐quality absorber with low‐point defects. And the CZTSSe solar cell with a PCE of 13.77% is successfully achieved. High‐crystalline‐quality absorbers with fewer defects are crucial for further improvement of open‐circuit voltage (VOC) and efficiency of Cu2ZnSn(S,Se)4 (CZTSSe) solar cells. However, the preparation of high‐quality CZTSSe absorbers remains challenging due to the uncontrollability of the selenization reaction and the complexity of the required selenization environment for film growth. Herein, a novel segmented control strategy for the selenization environment, specifically targeting the evaporation area of Se, to regulate the selenization reactions and improve the absorber quality is proposed. The large evaporation area of Se in the initial stage of the selenization provides a great evaporation and diffusion flux for Se, which facilitates rapid phase transition reactions and enables the attainment of a single‐layer thin film. The reduced evaporation area of Se in the later stage creates a soft‐selenization environment for grain growth, effectively suppressing the loss of Sn and promoting element homogenization. Consequently, the mitigation of Sn‐related deep‐level defects on the surface and in the bulk induced by element imbalance is simultaneously achieved. This leads to a significant improvement in nonradiative recombination suppression and carrier collection enhancement, thereby enhancing the VOC. As a result, the CZTSSe device delivers an impressive efficiency of 13.77% with a low VOC deficit.

A Robust Approach to Fabricate CZTSSe Absorber Layer for Solar Cells Via a Self-Selenizations Process Conducted by Concentrated Selenium Solution

Improving the Performance of Solution-Based CZTSSe Absorber by Selenization Annealing with Selenium Powder in Argon

Segmented Control of Selenization Environment for High‐Quality Cu2ZnSn(S,Se)4 Films Toward Efficient Kesterite Solar Cells

Low-cost Fabrication of Cu 2 ZnSnS 4 Thin Films for Solar Cell Absorber Layers

Passivation of Deep‐Level Defects through Chemical Environment Regulation for Efficient CZTSSe Solar Cells Based on Active Selenium Adsorption–Desorption Process

10.24% Efficiency of Flexible Cu2 ZnSn(S,Se)4 Solar Cells by Pre-Evaporation Selenization Technique

Controlling selenization equilibrium enables high-quality Cu2ZnSn(S, Se)4 absorbers for efficient solar cells

The enhancement of CZTSSe solar cell performance through active construction of the double-layer absorber

Achieving 11.95% Efficient Cu2ZnSnSe4 Solar Cells Fabricated by Sputtering a Cu-Zn-Sn-Se Quaternary Compound Target with a Selenization Process

Cu2ZnSnSSe4 Solar Cells with 9.6% Efficiency Via Selenizing Cu-Zn-Sn-S Precursor Sputtered from a Quaternary Target

CZTSSe solar cell with an efficiency of 10.19% based on absorbers with homogeneous composition and structure using a novel two-step annealing process

CZTSe solar cells prepared by electrodeposition of Cu/Sn/Zn stack layer followed by selenization at low Se pressure

Preparing Cu2ZnSnSe4 thin film solar cells based on selenium containing precursors

Exploring the optimal two-step selenization process to enhance the performance of ionic liquid solution based Cu2ZnSn(S,Se)4 thin film solar cells

Regulating Hetero‐Nucleation Enabling Over 14% Efficient Kesterite Solar Cells

Using Cu–Zn–Sn–O Precursor to Optimize CZTSSe Thin Films Fabricated by Se Doping With CZTS Thin Films

Beyond 10% Efficient CZTSSe Thin-Film Solar Cells Fabricated by a Two-Step CdS Deposition Process

Unveiling the Selenization Reaction Mechanisms in Ambient Air-Processed Highly Efficient Kesterite Solar Cells

Cu2ZnSn(S, Se)4 solar cell with slight band tailing states achieves 11.83% efficiency by selenizing sputtered Cu–Zn–Sn–S precursor

Significantly Improving the Crystal Growth of a Cu 2 ZnSn(S,Se) 4 Absorber Layer by Air-Annealing a Cu 2 ZnSnS 4 Precursor Thin Film

Microenvironment Created by SnSe2 Vapor and Pre‐Selenization to Stabilize the Surface and Back Contact in Kesterite Solar Cells