Abstract:Due to the various structural and functional characteristics of lightweight, energy absorption and sound/heat insulation et al, metallic foam materials have been increasingly developed in recent years, especially for the most widely used alloy foams. In this work, the Al‐Mg‐Si alloy foams with a porosity of 60% were prepared by a powder metallurgy technology, in which the carbamide was used as the space‐holder material. The effect of solution treatment on the microstructure, compressive property and energy absorption response of the as‐prepared Al‐Mg‐Si alloy foams was studied. The results show that when the solution temperature (T) is increased from 25 to 555 ℃, the room‐temperature compressive strength of the Al‐Mg‐Si alloy foams increases from 11.2 to 26.7 MPa, but decreases when T is more than 555 ℃. The strengthening mechanisms of solution treatment mainly lie in that the dislocation movement between the grain boundaries can be effectively blocked by the precipitated phases. Regarding to the high‐temperature compressive property of the Al‐Mg‐Si alloy foams that solution‐treated at 555 ℃, the compressive strength is found decrease from 28.7 to 12.3 MPa when the compression temperature is elevated up to 250 ℃. Correspondingly, the energy absorption decreases from 17.02 to 9.14 MJ/m3. Compared to the pure Al foam, the high‐temperature softening effect for the Al‐Mg‐Si alloy foams is more remarkable, which ascribes to the formation of microcracks in the alloy matrix. The current research provides us a cost‐effective and easy‐handle approach to enhance the compressive strength and energy absorption ability of the metallic foam materials.This article is protected by copyright. All rights reserved.

Multifunctional Foaming Agent to Prepare Aluminum Foam with Enhanced Mechanical Properties

Effect of Cu and Sn Additions on the Cellular Structure of Al–Si–Mg Alloys Foaming at Low Temperature (≤600 °C)

Optimizing Calcium Addition for Fabricating Aluminum Foams with Different Pore Sizes

Development of AlMg35-TiH2 composite foaming agent and fabrication of small pore size aluminium foams

Foaming Process and Properties of 6063 Aluminum Foams by Melt Foaming Method

Controllable Design of Structural and Mechanical Behaviors of Al‐Si Foams by Powder Metallurgy Foaming

Foamability and mechanical properties of in situ submicron MgAl2O4p/Al composite foams by ultrasonic method

Optimization of Cellular Structure of Aluminum Foams Produced by Powder Metallurgy Method

Fabrication of Cu-Mg alloy foam with close pore structure by gas release reaction powder metallurgical approach

Foaming Behavior of AlMg4Si8 Matrix and Pure Al Matrix Precursors in Closed Cavities with Different TiH2 Addition Levels

Fabrication of Mg-Al Alloy Foam with Close-Cell Structure by Powder Metallurgy Approach and Its Mechanical Properties

Enhancement of the Mechanical Strength of Aluminum Foams by SiC Nanoparticles

Effect of calcium addition on the aluminum alloy A201 foam

Fabrication of Uniform and Rounded Closed-Cell Aluminum Foams Using Novel Foamable Precursor Particles (FPPs)

Effect of Heat Treatment on the Microstructure, Compressive Property, and Energy Absorption Response of the Al–Mg–Si Alloy Foams

Optimization of Mg Blowing Agent Content for Foaming Aluminum

Study on an Aluminum Foam by Gas Injection Foaming

Enhanced Mechanical Properties of Novel Aluminum Foams Synergistically Reinforced by NiO Particles and in Situ Grown Carbon Nanotubes

Ultralight Alumina Ceramic Foams with Single-Grain Wall Using Sodium Dodecyl Sulfate As Long-Chain Surfactant

Aluminum Foam Sandwich: Pore Evolution Mechanism Investigation and Engineering Preparing Optimization

Preparation and Compressive Performance of an A356 Matrix Syntactic Foam