Microstructure and Mechanical Properties of TiCp/Mg-4Zn-0.5Ca Nanocomposite in Different Processing Conditions

K. B. Nie,Y. C. Guo,K. K. Deng,X. K. Kang

DOI: https://doi.org/10.1088/2053-1591/ab0cd6

IF: 2.025

2019-01-01

Materials Research Express

Abstract:Mg-4Zn-0.5Ca matrix composite reinforced by nano-sized TiC particle was successfully prepared for the first time. The as-cast TiCp/Mg-4Zn-0.5Ca nanocomposites were then extruded at 270 °C and different extrusion speeds. The decreased grain size for the as-cast nanocomposite was due to that the added TiC nanoparticles could act as the nucleation sites for new grains and hinder the grain growth by pinning the grain boundaries during the solidification process. The tensile properties for the as-cast nanocomposites fabricated at different ultrasonic temperatures were affected by the distribution state of the TiC nanoparticles. The average recrystallized grain size of the TiCp/Mg-4Zn-0.5Ca nanocomposite was larger than the Mg-4Zn-0.5Ca alloy with or without the addition of micro-sized particles extruded at the same conditions. This indicated that pin effect of the present TiC nanoparticles in the grain boundary was weaker than the grain growth induced by plastic deformation. The yield strength, ultimate tensile strength and elongation of the TiCp/Mg-4Zn-0.5Ca nanocomposite extruded at 0.01 mm s−1 were ∼228 MPa, ∼294 MPa and ∼21%, respectively. The superior ductility as well as comparable tensile strength could be mainly associated with high recrystallization rate, relatively coarse grains, precipitated MgZn2 phases and the added TiC nanoparticles.