Abstract:High strength and high toughness are important indicators of material load-bearing capacity and reliability. The challenge remains on how to improve the material strength while maintaining its toughness during conventional surface treatments, such as overall hardening. This paper proposed a multi-pass discrete laser spot hardening (DLSH) process based on time-domain energy modulation. The characteristics of 42CrMoV alloy steel treated with multi-pass DLSH process, compared with conventional DLSH process, were investigated in terms of surface quality, microstructure evolution, and tensile properties. The results demonstrated that the surface quality of the hardened point lattice using multi-pass processing was significantly improved, and the microstructure was refined after multiple rapid austenitization cycles. Additionally, different "soft-hard" distribution states were formed on the sample surface. The ultimate tensile strength of the samples treated with conventional DLSH and multi-pass DLSH processes was increased by 9.5% and 5.2% respectively. However, the latter exhibited significantly higher elongation at fracture and showed a ductile fracture, while the former displayed brittle fracture. The multi-pass DLSH process maintained the original material toughness while enhancing its strength. Therefore, the multi-pass DLSH process holds significant importance in improving surface quality and material toughness in laser hardening applications.

Investigation of Ductile Damage Induced by Laser Shock Processing on a 35CD4 Steel

Prediction and Characterization of Plastic Damage in a Weld Joint Resulting from Laser Shock Processing

Redistribution of Residual Stress Field in the Weld Joint Due to Laser Shock Processing

Study on numerical simulation of residual stresses induced by laser shock processing

Mitigation of Tensile Residual Stress Induced During Welding with Laser Shock Processing

3-D FEM simulation of laser shock processing

Simulation of the elasto-plastic response and residual stresses near metal surface due to laser shock processing

Ductile Damage Analysis for Small Punch Specimens of Type 304 Stainless Steel Based on GTN Model

Residual Stress Field Induced by Laser Peening: a Finite Element Analysis

Effects of Laser Shock Processing on Morphologies and Mechanical Properties of ANSI 304 Stainless Steel Weldments Subjected to Cavitation Erosion

Numerical investigation on spall fracture in a metallic material caused by laser shock peening

Effect of distribution status of the spot matrix on tensile behavior for 42CrMoV when conducting discrete laser surface strengthening: Based on experiment and simulation

Plastic Deformation Mechanisms and Their Threshold Pressures of Ti6Al4V Thin-Walled Structures Induced by Laser Peen Forming

Damage characterization and discrimination in laser-shocked carbon fiber reinforced polymer laminates: A mass-spring-damping model approach

Morphology characteristics of several metallic structural materials under laser shock

Effect of surface nanocrystallization produced by laser shock processing on the corrosion fatigue behavior of 300M steel

High Cycle Fatigue Performance in Laser Shock Peened TC4 Titanium Alloys Subjected to Foreign Object Damage

Dynamic Response and Residual Stress Fields of Ti6al4v Alloy under Shock Wave Induced by Laser Shock Peening

Experimental techniques for ductile damage characterisation

Comparison of Two Uncoupled Ductile Damage Initiation Models Applied to DP900 Steel Sheet under Various Loading Paths

Mechanical Properties and Tensile Failure Mechanisms of SM400A Steel Treated by High-Power Continuous-Wave Laser