Abstract:Dry reforming of methane (DRM) is one of the most valuable ways to convert carbon dioxide (CO2) and methane (CH4) simultaneously. Although Ni-based catalysts have been widely used due to their high activity and low cost, the problems with sintering and carbon deposition have consistently limited their large-scale industrial applications. In this work, based on the high surface area and excellent adsorption capacity of porous Al2O3 material, three kinds of rod-like Ni- Al2O3 catalysts (Ni- Al2O3-500, Ni-Al2O3-700, Ni-Al2O3-900) were successfully synthesized by impregnation strategy and calcination at 500, 700 and 900 °C respectively. During the 60-h stability test, the conversions of CH4 and CO2 catalyzed by the Ni-Al2O3-700 catalyst with 3% Ni was consistently maintained at around 60.0% and 65.0%, respectively, with only 5.8% residual carbon on the catalyst surface. According to the analysis of Temperature programmed reduction (H2-TPR), X-ray photoelectron spectroscopy (XPS), Temperature programmed deposition (CO-TPD) and the test results, the influence of calcination temperature on the catalytic performance of Ni-Al2O3 catalyst was comprehensively studied. Under different calcination temperatures, the interaction between Ni species and porous Al2O3 support was successfully regulated. Different from introducing more favorable chemical components to the catalyst system, this work created a rod-like Ni-Al2O3-700 catalyst with excellent resistance to carbon deposition and sintering and a higher ratio of Ni0/Ni2+ (0.044) based on the calcination temperature and the changes of microstructure during the phase transition of Al2O3 materials, which provided a new strategy for constructing a structured and high-performance Ni-based catalyst.

Autothermal Reforming and Partial Oxidation of Methane in Fluidized Reactor over Highly Dispersed Ni Catalyst Prepared from Ni Complex

Combined Carbon Dioxide Reforming and Partial Oxidation of Methane to Syngas over Ni−La2O3/SiO2 Catalysts in a Fluidized-Bed Reactor

Catalytic conversion of methane and CO2 to synthesis gas over a La2O3-modified SiO2 supported Ni catalyst in fluidized-bed reactor

Combined Catalytic Partial Oxidation and CO2 Reforming of Methane over ZrO2-modified Ni/SiO2 Catalysts Using Fluidized-Bed Reactor

Autothermal Reforming of CH4 and C3H8 to Syngas in a Fluidized-Bed Reactor

Deactivation of Ni Catalysts During Methane Autothermal Reforming with CO2 and O2 in a Fluidized-Bed Reactor

Combined Carbon Dioxide Reforming and Partial Oxidation of Methane to Syngas over Ni−La<sub>2</sub>O<sub>3</sub>/SiO<sub>2</sub>Catalysts in a Fluidized-Bed Reactor

Syngas Production from Reforming of Methane with Co2 and O-2 over Ni/Sro-Sio2 Catalysts in A Fluidized Bed Reactor

Preparation of Nickel-Foam-supported Pd/NiO Monolithic Catalyst and Construction of Novel Electric Heating Reactor for Catalytic Combustion of VOCs

Combination of CO2 Reforming and Partial Oxidation of Methane over Ni/BaO-SiO2 Catalysts to Produce Low H2/CO Ratio Syngas Using a Fluidized Bed Reactor

Syngas Production Via Combined Oxy-Co2 Reforming of Methane over Gd2O3-modified Ni/SiO2 Catalysts in a Fluidized-Bed Reactor

Fabrication of CeZrO2 on Ni/SiO2 and Promoted Catalysis for Methane Autothermal Reforming in a Fluidized Bed Reactor

Highly Dispersed Ni Nanoparticles Supported by Porous Al2O3 Rods for Catalytic Dry Reforming of Methane

Partial Oxidation Of Methane To Syngas Over Ni-Based Catalysts

Synthesis of Highly-Dispersed Ni/Mesoporous Silica Via an Ammonia Evaporation Method for Dry Reforming of Methane: Effect of the Ni Loadings

Template in situ inducing dispersion of nickel on SBA-15 for methane reforming with carbon dioxide

Catalytic Performance of Ni/SiO2 in Converting Methane to Syngas Using Fluidized Bed Reactor

Highly dispersed Ni/MgO-mSiO2 catalysts with excellent activity and stability for dry reforming of methane

Ni/SiO2 Catalyst Prepared by Strong Electrostatic Adsorption for a Low-Temperature Methane Dry Reforming Reaction

Catalytic Performance of Ni/CaO-SiO2 for Converting Methane to Syngas in A Fluidized Bed Reactor

Ni/SiO2 Catalyst Prepared with Nickel Nitrate Precursor for Combination of CO2 Reforming and Partial Oxidation of Methane: Characterization and Deactivation Mechanism Investigation